Samsung Cheil Industries Infino® CF-3200HF PC, Glass Filled High Impact

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® CF-3200HF PC, Glass Filled High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Water Absorption 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 ASTM D570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 23 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 23 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Tensile Strength, Yield 98.1 MPa
14200 psi
5 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
2.8 mm/min; ASTM D790
Flexural Modulus 5.49 GPa
797 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.86 J/cm

@Thickness 3.17 mm
 3.49 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 141 °C

@Thickness 6.40 mm
 286 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 137 °C
279 °F
B/50; ISO R306
Flammability, UL94 2.00

@Thickness 3.20 mm
 2.00

@Thickness 0.126 in
V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in