- Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled
Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy + GF , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT/ABS with 20% GF reinforcement that can be used in air-conditioner bladesInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Temperature 23.0 °C |
0.080 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 33 g/10 min @Load 5.00 kg, Temperature 250 °C |
33 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Ash | 19 % | 19 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 78.5 MPa | 11400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 78.5 MPa | 11400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.90 GPa | 711 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.647 J/cm @Thickness 6.35 mm |
1.21 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.647 J/cm @Thickness 3.17 mm |
1.21 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 6.40 mm |
401 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | B/50; ISO R306 |
| 131 °C | 268 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Delrin® 100AF Acetal Homopolymer (Unverified Data**)
- DSM Akulon® K230-HXG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond) (discontinued **)
- LG Chemical LGflex BET Plasticizer
- Momentive Performance Materials Siloprenâ„¢ LSR 2735/30 Liquid Silicone Rubber - Self-Bonding / Self-Lubricating
- LyondellBasell Astryn SD068-4 Polypropylene Copolymer, 40% Calcium Carbonate
- Stellarchem 475-860N TPE Compound
- Dow Corning SYL-OFF® 7677 RELEASE COATING
- Entec Hypro™ PPH-GF40 Natural Homopolymer Polypropylene, 40% Glass Reinforced
- Abatron Abosolv™ General Purpose Thinner and Solvent
- Americas Styrenics MC3650 High Heat Crystal Polystyrene
Copyright © lookpolymers.com All Rights Reserved