Samsung Cheil Industries Infino® NH-1001T PC/ABS, Unreinforced FR

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® NH-1001T PC/ABS, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Melt Flow 26 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 26 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength at Break 52.0 MPa
7540 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 56.9 MPa
8250 psi
50 mm/min; ASTM D638
Elongation at Break 87 %
87 %
50 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
327 ksi
50 mm/min; ASTM D638
Flexural Strength 83.4 MPa
12100 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.45 GPa
356 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 5.20 J/cm

@Thickness 6.35 mm
 9.74 ft-lb/in

@Thickness 0.250 in
 ASTM D256
7.16 J/cm

@Thickness 3.17 mm
 13.4 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C

@Thickness 6.40 mm
 183 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 94.0 °C
201 °F
B/50; ISO R306
95.0 °C
203 °F
B/120; ISO R306
Flammability, UL94 V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in