Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Temperature 23.0 °C |
0.070 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.011 cm/cm @Thickness 3.20 mm |
0.0040 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 250 °C |
21 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Ash | 15 % | 15 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 82.4 MPa | 12000 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 83.4 MPa | 12100 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.61 GPa | 668 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 5.79 GPa | 839 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.275 J/cm @Thickness 3.17 mm |
0.514 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 0.333 J/cm @Thickness 6.35 mm |
0.625 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C @Thickness 6.40 mm |
381 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 202 °C | 396 °F | B/50; ISO R306 |
| 206 °C | 403 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 0.740 - 3.00 mm |
V-0 @Thickness 0.0291 - 0.118 in |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy® 10 Pb-In Solder Alloy
- Solvay Chemicals CASO® TEC SOLUTION 25-29% Calcium Chloride
- Styrolution Styrolux® GH 62 SBC
- A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
- A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6
- Tra-Con Tra-Bond 2143G Medium Viscosity Polyamide Epoxy Adhesive
- A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy
- Chengdu Polyster H8570 Thermoplastic Polyether-ester Elastomer (TPEE)
- Aclo Accutech Polypropylene Homopolymer HP0334C30L1 Calcium Reinforced
- HP Alloys Alloy 718, 5% Cold Worked
Copyright © lookpolymers.com All Rights Reserved