Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 216 MPa | 31300 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 11.3 GPa | 1640 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 - 3.00 mm |
V-0 @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- Niche Polymer PA66GF50BK Nylon 66, 50% Glass Fiber Filled
- Resin Technology Group 395 Plastics, Large Gap Fill Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- Polykemi AB POLYfill PPH T20020 UV Polypropylene Homopolymer, Mineral Reinforced, UV-Stabilized
- Hexion Bakelite™ PF 1141 Phenolic Formaldehyde Resin, High Surface Quality, Resistant to High Temperatures, Dishwasher Proof
- H.C. Starck Amperit® 544.059 Dense Coated Tungsten Carbide-Nickel 83-17 (WC-Ni)
- A. Schulman FORMION™ FI 389 Ionomer
- Arlon Thermabond® 48A51X015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Huntsman PE2050 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved