Samsung Cheil Industries StarexÂ® LX-0957 ABS, Unreinforced Metallic-Look

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	Samsung, Cheil Industries
Trade Name	Starex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samsung Cheil Industries StarexÂ® LX-0957 ABS, Unreinforced Metallic-Look.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Melt Flow	12 g/10 min @Load 10.0 kg, Temperature 220 Â°C	12 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	111	111	ASTM D785
Tensile Strength at Break	38.2 MPa	5540 psi	5 mm/min; ASTM D638
Tensile Strength, Yield	45.1 MPa	6540 psi	5 mm/min; ASTM D638
Elongation at Break	31 %	31 %	5 mm/min; ASTM D638
Tensile Modulus	2.16 GPa	313 ksi	5 mm/min; ASTM D638
Flexural Strength	68.6 MPa	9950 psi	2.8 mm/min; ASTM D790
Flexural Modulus	2.55 GPa	370 ksi	2.8 mm/min; ASTM D790
Izod Impact, Notched	1.47 J/cm @Thickness 6.35 mm	2.76 ft-lb/in @Thickness 0.250 in	ASTM D256
	1.67 J/cm @Thickness 3.17 mm	3.12 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	94.0 Â°C @Thickness 6.40 mm	201 Â°F @Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	85.0 Â°C @Thickness 6.40 mm	185 Â°F @Thickness 0.252 in	ASTM D648
Vicat Softening Point	95.0 Â°C	203 Â°F	B/50; ISO R306
	102 Â°C	216 Â°F	B/120; ISO R306
Flammability, UL94	HB @Thickness 1.20 - 1.32 mm	HB @Thickness 0.0472 - 0.0520 in