Samyang Triel® 5722EM Thermoplastics Polyetherester Elastomer, Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5722EM Thermoplastics Polyetherester Elastomer, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5722EM is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 18 - 22 g/10 min @Load 2.16 kg, Temperature 240 °C |
18 - 22 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength, Ultimate | 41.7 MPa | 6040 psi | ASTM D638 |
| Flexural Yield Strength | 36.3 MPa | 5260 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 - 1.27 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.84 - 2.39 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.96 - 2.45 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
3.67 - 4.59 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ASTM D648 |
| Vicat Softening Point | 205 °C | 401 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJAF111L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polycasa Acryl® G 77 E Acrylic, Extrusion Grade
- Lanxess Pocan® BF 4215 000000 PBT, 12% Glass Fiber
- TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Beta Forged
- Wanhua Chemical Wanthane® WHT-8180 Polyether-Based TPU
- Lubrizol ESTANE® 5715 Ester Based Thermoplastic Polyurethane
- Entec Hypel® PEHD30/.950 HDPE
- Aclo Accutech Polypropylene Copolymer CP0437T20L1 Talc Reinforced
- 3M 5010 Polyurethane Multi-Purpose Adhesive
Copyright © lookpolymers.com All Rights Reserved