Sax Polymers SAXAMID 226F5 Nylon 6.6, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226F5 Nylon 6.6, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226F5 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 25% glass fibers. It has high mechanical strength in combination with good flow properties.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 175 MPa | 25400 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 8.60 GPa | 1250 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 250 MPa | 36300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 250 °C | 482 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ G1550S High Performance Polypropylene Nanocomposite
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled
- Freudenberg Simrit V75 Standard Fluoroelastomer
- Tipco Tipcolite® TPF 1011 - Unreinforced Thermoset Phenolic Resin, 43 mm Norton Flow without Hexamine
- A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6
- Dow SPECFLEX™ NC 638 Polyol
- DuPont Teijin Films Melinex® HS2 Polyester Film
- Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (9 mm Molded Thickness)
- BASF Elastollan 590 A TPUR
Copyright © lookpolymers.com All Rights Reserved