Seals Eastern 5722A Fluorocarbon-Elastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Seals Eastern, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 5722A Fluorocarbon-Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Seals Eastern's formulated Viton® elastomers can be utilized in seals, o-rings, gaskets, packings and other applications where thermal stability and chemical resistance are required.Features:Excellent mechanical propertiesGood extrusion resistanceChemical and heat resistantType 1 (Viton A)Viton® is a registered trademark of DuPont. Information provided by Seals Eastern.
Physical Properties Metric English Comments
Specific Gravity 1.84 g/cc
1.84 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 56
>= 56
ASTM D2240
62
62
Dry Heat Aging 392°F; 1000 hr; ASTM D865
62
62
Dry Heat Aging 392°F; 336 hr; ASTM D865
62
62
Average; ASTM D2240
63
63
Dry Heat Aging 392°F; 168 hr; ASTM D865
63
63
Dry Heat Aging 392°F; 70 hr; ASTM D865
Tensile Strength >= 5.29 MPa
>= 767 psi
ASTM D412 Method A
7.963 MPa
1155 psi
Average; ASTM D412 Method A
8.363 MPa
1213 psi
Dry Heat Aging 392°F; 70 hr; ASTM D865
9.556 MPa
1386 psi
Dry Heat Aging 392°F; 1000 hr; ASTM D865
9.797 MPa
1421 psi
Dry Heat Aging 392°F; 336 hr; ASTM D865
9.873 MPa
1432 psi
Dry Heat Aging 392°F; 168 hr; ASTM D865
Tensile Stress >= 0.951 MPa

@Strain 50.0 %
>= 138 psi

@Strain 50.0 %
ASTM D412 Method A
1.05 MPa

@Strain 25.0 %
152 psi

@Strain 25.0 %
Average; ASTM D412 Method A
1.48 MPa

@Strain 50.0 %
214 psi

@Strain 50.0 %
Average; ASTM D412 Method A
>= 1.58 MPa

@Strain 100 %
>= 229 psi

@Strain 100 %
ASTM D412 Method A
2.22 MPa

@Strain 100 %
322 psi

@Strain 100 %
Average; ASTM D412 Method A
Elongation at Break >= 180 %
>= 180 %
ASTM D412 Method A
294 %
294 %
Dry Heat Aging 392°F; 1000 hr; ASTM D865
320 %
320 %
Average; ASTM D412 Method A
326 %
326 %
Dry Heat Aging 392°F; 336 hr; ASTM D865
336 %
336 %
Dry Heat Aging 392°F; 70 hr; ASTM D865
342 %
342 %
Dry Heat Aging 392°F; 168 hr; ASTM D865
Modulus of Elasticity 0.007370 GPa
1.069 ksi
Calculated; ASTM D412 Method A
Shear Modulus 0.00245 GPa
0.356 ksi
Calculated; ASTM D412 Method A
Secant Modulus 0.006929 GPa
1.005 ksi
ASTM D412 Method A
Tear Strength Test 141
141
psi; ASTM D624, Die B
Compression Set 19 %

@Temperature 200 °C,
Time 79200 sec
19 %

@Temperature 392 °F,
Time 22.0 hour
ASTM D395, Test B
23 %

@Temperature 200 °C,
Time 252000 sec
23 %

@Temperature 392 °F,
Time 70.0 hour
ASTM D395, Test B
39 %

@Temperature 200 °C,
Time 1.21e+6 sec
39 %

@Temperature 392 °F,
Time 336 hour
ASTM D395, Test B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
400 °F
Glass Transition Temp, Tg -20.0 °C
-4.00 °F
ASTM D1329
Processing Properties Metric English Comments
Shelf Life 180 Month
180 Month
Descriptive Properties Value Comments
Strain Energy/ Unit Volume at 20% Elongation (psi) 19
ASTM D412 Method A