Shanghai Ofluorine J-2 PVDF Extrusion Grade

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer Shanghai Ofluorine
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shanghai Ofluorine J-2 PVDF Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: J-2 PVDF is a kind of granules homopolymer, which has middle melt viscosity, J-2 is more suitable for extrusion process. J-2 PVDF pellets as raw materials, the finished products has excellent mechanical strength and flexibility. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100°C, which keep stable. Others, J-2 PVDF finished products has the properties of ?-Ray resistant, UV resistant, and stability in wide temperature range. Application: manufacture PVDF tubes, PVDF pipes, PVDF valves etc.Information provided by Shanghai Ofluorine Chemical Technology
Physical Properties Metric English Comments
Specific Gravity 1.77 - 1.79 g/cc
1.77 - 1.79 g/cc
ASTM D792
Water Absorption <= 0.050 %
<= 0.050 %
ASTM D570
Melt Flow 5.0 - 10 g/10 min

@Load 10.0 kg,
Temperature 230 °C
5.0 - 10 g/10 min

@Load 22.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 70 - 80
70 - 80
ASTM D2240
Tensile Strength at Break >= 30.0 MPa
>= 4350 psi
50mm/min; ASTM D638
Tensile Strength, Yield >= 40.0 MPa
>= 5800 psi
50mm/min; ASTM D638
Elongation at Break >= 50 %
>= 50 %
50mm/min; ASTM D638
Elongation at Yield 5.0 - 10 %
5.0 - 10 %
50mm/min; ASTM D638
Thermal Properties Metric English Comments
Melting Point 165 - 171 °C
329 - 340 °F
10°C/min; ASTM D3418
Flammability, UL94 V-0
V-0
Descriptive Properties Value Comments
Appearance White translucent pellets