Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded  

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded  .pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. AMODEL A-1115 HS resin can be easily processed using conventional equipment and methods.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.MatWeb has an entry for this material conditioned at 50% RH.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ASTM D792
Water Absorption 0.30 %
0.30 %
24 hrs. ASTM D570
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 127
127
ASTM D785
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Flexural Yield Strength 171 MPa
24800 psi
ASTM D790
Flexural Modulus 6.20 GPa
899 ksi
ASTM D790
Compressive Yield Strength 207 MPa
30000 psi
ASTM D695
Poissons Ratio 0.41
0.41
Shear Modulus 2.94 GPa
426 ksi
Calculated
Shear Strength 88.0 MPa
12800 psi
ASTM D732
Izod Impact, Notched 0.440 J/cm
0.824 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.38 J/cm
8.21 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 12.0 µm/m-°C

@Temperature 160 - 250 °C
6.67 µin/in-°F

@Temperature 320 - 482 °F
FD; ASTM E831
35.0 µm/m-°C

@Temperature 0.000 - 100 °C
19.4 µin/in-°F

@Temperature 32.0 - 212 °F
FD; ASTM E831
95.0 µm/m-°C

@Temperature 160 - 250 °C
52.8 µin/in-°F

@Temperature 320 - 482 °F
TD; ASTM E831
CTE, linear, Transverse to Flow 59.0 µm/m-°C

@Temperature 0.000 - 100 °C
32.8 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E381
Melting Point 310 °C
590 °F
ASTM D3418
Maximum Service Temperature, Air 160 °C
320 °F
20,000 hours continuous use; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi) 292 °C
558 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
ASTM D648
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.9

@Frequency 1e+6 Hz
3.9

@Frequency 1e+6 Hz
ASTM D150
4.2

@Frequency 60 Hz
4.2

@Frequency 60 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Dissipation Factor 0.0060

@Frequency 60 Hz
0.0060

@Frequency 60 Hz
ASTM D150
0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 130 sec
130 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
Processing Properties Metric English Comments
Melt Temperature 321 - 343 °C
610 - 649 °F
Injection