Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA), 33% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® A-1133 NL resin is a 33% glass reinforced polyphthalamide (PPA) which is distinguished by its high-reflectivity white color. This grade features a high deflection temperature for compatibility with SMT processes, and low moisture absorption.Features: Good Chemical Resistance; Good Color Stability; High Reflectivity; Low Moisture AbsorptionUses: Automotive Electronics; Housings; LEDsInjection Molding Notes: A general purpose screw is recommended, with minimum back pressure.Automotive Specifications ASTM D6779 PA128G35Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.16 %

@Time 86400 sec
0.16 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D785
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
Elongation at Break 1.8 %
1.8 %
ASTM D638
Tensile Modulus 12.4 GPa
1800 ksi
ASTM D638
Flexural Yield Strength 236 MPa
34200 psi
ASTM D790
Flexural Modulus 11.7 GPa
1700 ksi
ASTM D790
Poissons Ratio 0.41
0.41
ASTM E132
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C

@Temperature 160 - 250 °C
7.78 µin/in-°F

@Temperature 320 - 482 °F
2
23.0 µm/m-°C

@Temperature 0.000 - 100 °C
12.8 µin/in-°F

@Temperature 32.0 - 212 °F
2
CTE, linear, Transverse to Flow 45.0 µm/m-°C

@Temperature 0.000 - 100 °C
25.0 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
100 µm/m-°C

@Temperature 100 - 250 °C
55.6 µin/in-°F

@Temperature 212 - 482 °F
TMA; ASTM E831
Melting Point 310 °C
590 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 271 °C
520 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color White
Form Pellets
Processing Technique Injection Molding