Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. - Black: A-1145 HS BK 324 - Natural: A-1145 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
ISO 1183/A
Filler Content 45 %
45 %
Glass Fiber Reinforcement
Water Absorption 0.12 %

@Time 86400 sec
0.12 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Conditioned; ASTM D955
0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Conditioned; ASTM D955
0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
R-Scale; ASTM D785
Tensile Strength at Break 75.8 MPa

@Temperature 175 °C
11000 psi

@Temperature 347 °F
ISO 527-2
84.8 MPa

@Temperature 150 °C
12300 psi

@Temperature 302 °F
ISO 527-2
173 MPa

@Temperature 100 °C
25100 psi

@Temperature 212 °F
ISO 527-2
263 MPa

@Temperature 23.0 °C
38100 psi

@Temperature 73.4 °F
ISO 527-2
Tensile Strength 228 MPa
33100 psi
Conditioned; ASTM D638
259 MPa
37600 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
Conditioned; ASTM D638
2.6 %
2.6 %
ASTM D638
2.5 %

@Temperature 100 °C
2.5 %

@Temperature 212 °F
ISO 527-2
2.7 %

@Temperature 23.0 °C
2.7 %

@Temperature 73.4 °F
ISO 527-2
6.5 %

@Temperature 175 °C
6.5 %

@Temperature 347 °F
ISO 527-2
7.2 %

@Temperature 150 °C
7.2 %

@Temperature 302 °F
ISO 527-2
Tensile Modulus 17.2 GPa
2490 ksi
Conditioned; ASTM D638
17.2 GPa
2490 ksi
ASTM D638
5.38 GPa

@Temperature 175 °C
780 ksi

@Temperature 347 °F
ISO 527-2
8.00 GPa

@Temperature 150 °C
1160 ksi

@Temperature 302 °F
ISO 527-2
11.2 GPa

@Temperature 100 °C
1620 ksi

@Temperature 212 °F
ISO 527-2
16.8 GPa

@Temperature 23.0 °C
2440 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 294 MPa
42600 psi
Conditioned; ASTM D790
363 MPa
52600 psi
ASTM D790
94.5 MPa

@Temperature 175 °C
13700 psi

@Temperature 347 °F
ISO 178
111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
ISO 178
267 MPa

@Temperature 100 °C
38700 psi

@Temperature 212 °F
ISO 178
377 MPa

@Temperature 23.0 °C
54700 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 13.8 GPa
2000 ksi
Conditioned; ASTM D790
13.8 GPa
2000 ksi
ASTM D790
4.90 GPa

@Temperature 175 °C
711 ksi

@Temperature 347 °F
ISO 178
5.38 GPa

@Temperature 150 °C
780 ksi

@Temperature 302 °F
ISO 178
13.0 GPa

@Temperature 100 °C
1890 ksi

@Temperature 212 °F
ISO 178
15.9 GPa

@Temperature 23.0 °C
2310 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 194 MPa

@Thickness 25.4 mm
28100 psi

@Thickness 1.00 in
ASTM D695
Poissons Ratio 0.41
0.41
ASTM E132
Shear Modulus 5.96 - 6.10 GPa
864 - 885 ksi
Calculated
Shear Strength 91.7 MPa
13300 psi
Conditioned; ASTM D732
108 MPa
15700 psi
ASTM D732
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
Conditioned; ASTM D256
1.10 J/cm
2.06 ft-lb/in
ASTM D256
11.0 J/cm
20.6 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 61.0 kJ/m²

@Temperature 23.0 °C
29.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 9.20 J/cm²
43.8 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C

@Temperature 0.000 - 100 °C
7.78 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
35.0 µm/m-°C

@Temperature 100 - 200 °C
19.4 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 0.000 - 100 °C
27.8 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
150 µm/m-°C

@Temperature 100 - 200 °C
83.3 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 310 °C
590 °F
Peak; ASTM D3418
310 °C
590 °F
ISO 11357-3
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
Conditioned; ASTM D257
1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 4.4

@Frequency 1.00e+6 Hz
4.4

@Frequency 1.00e+6 Hz
ASTM D150
4.5

@Frequency 1.00e+6 Hz
4.5

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
4.6

@Frequency 60.0 Hz
4.6

@Frequency 60.0 Hz
ASTM D150
4.9

@Frequency 60.0 Hz
4.9

@Frequency 60.0 Hz
Conditioned; ASTM D150
Dielectric Strength 23.0 kV/mm

@Thickness 3.20 mm
584 kV/in

@Thickness 0.126 in
Conditioned; ASTM D149
23.0 kV/mm

@Thickness 3.20 mm
584 kV/in

@Thickness 0.126 in
ASTM D149
Dissipation Factor 0.0050

@Frequency 60.0 Hz
0.0050

@Frequency 60.0 Hz
ASTM D150
0.0090

@Frequency 60.0 Hz
0.0090

@Frequency 60.0 Hz
Conditioned; ASTM D150
0.016

@Frequency 1.00e+6 Hz
0.016

@Frequency 1.00e+6 Hz
ASTM D150
0.021

@Frequency 1.00e+6 Hz
0.021

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
Arc Resistance 125 sec
125 sec
ASTM D495
145 sec
145 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
UL 746
550 V
550 V
UL 746