Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage. Excellent dimensional stability and low moisture absorption are also characteristics of this resin. AMODEL A-1340 HS resin can be easily processed using conventional equipment and methods.Information provided by Solvay Advanced Polymers

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ISO 1183A
	1.54 g/cc	1.54 g/cc	ASTM D792
Moisture Absorption at Equilibrium	0.16 %	0.16 %	24 hours; ASTM D570

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	125	125	ASTM D785
Tensile Strength, Yield	151 MPa	21900 psi	ISO 527
	174 MPa	25200 psi	ASTM D638
	46.0 MPa @Temperature 175 °C	6670 psi @Temperature 347 °F	ISO 527
	49.0 MPa @Temperature 150 °C	7110 psi @Temperature 302 °F	ISO 527
	97.0 MPa @Temperature 100 °C	14100 psi @Temperature 212 °F	ISO 527
Elongation at Break	1.8 %	1.8 %	ISO 527
	2.3 % @Temperature 100 °C	2.3 % @Temperature 212 °F	ISO 527
	7.0 % @Temperature 175 °C	7.0 % @Temperature 347 °F	ISO 527
	7.4 % @Temperature 150 °C	7.4 % @Temperature 302 °F	ISO 527
Elongation at Yield	2.2 %	2.2 %	ASTM D638
Tensile Modulus	11.0 GPa	1600 ksi	ASTM D638
	11.6 GPa	1680 ksi	ISO 527
	2.70 GPa @Temperature 175 °C	392 ksi @Temperature 347 °F	ISO 527
	3.10 GPa @Temperature 150 °C	450 ksi @Temperature 302 °F	ISO 527
	8.00 GPa @Temperature 100 °C	1160 ksi @Temperature 212 °F	ISO 527
Flexural Strength	234 MPa	33900 psi	ISO 178
	263 MPa	38100 psi	ASTM D790
	55.0 MPa @Temperature 175 °C	7980 psi @Temperature 347 °F	ISO 178
	63.0 MPa @Temperature 150 °C	9140 psi @Temperature 302 °F	ISO 178
	155 MPa @Temperature 100 °C	22500 psi @Temperature 212 °F	ISO 178
Flexural Modulus	9.10 GPa	1320 ksi	ISO 178
	10.6 GPa	1540 ksi	ASTM D790
	2.30 GPa @Temperature 175 °C	334 ksi @Temperature 347 °F	ISO 178
	2.50 GPa @Temperature 150 °C	363 ksi @Temperature 302 °F	ISO 178
	6.80 GPa @Temperature 100 °C	986 ksi @Temperature 212 °F	ISO 178
Poissons Ratio	0.38	0.38
Shear Modulus	3.99 - 4.20 GPa	579 - 609 ksi	Calculated
Shear Strength	91.0 MPa	13200 psi	ASTM D732
Izod Impact, Notched	0.450 J/cm	0.843 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	4.00 kJ/m²	1.90 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	31.0 kJ/m²	14.8 ft-lb/in²	ISO 180/1U
Charpy Impact Unnotched	4.50 J/cm²	21.4 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.330 J/cm²	1.57 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	19.0 µm/m-°C @Temperature 160 - 250 °C	10.6 µin/in-°F @Temperature 320 - 482 °F
	29.0 µm/m-°C @Temperature 0.000 - 100 °C	16.1 µin/in-°F @Temperature 32.0 - 212 °F
CTE, linear, Transverse to Flow	46.0 µm/m-°C @Temperature 0.000 - 100 °C	25.6 µin/in-°F @Temperature 32.0 - 212 °F
	92.0 µm/m-°C @Temperature 160 - 250 °C	51.1 µin/in-°F @Temperature 320 - 482 °F
Melting Point	313 °C	595 °F	ISO 11357-3
	313 °C	595 °F	ASTM D3418
Maximum Service Temperature, Air	130 °C	266 °F	20000 hours, Continuous; ASTM D3045
	150 °C	302 °F	5000 hours, Continuous; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi)	290 °C	554 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	262 °C	504 °F	ISO 75Af
	275 °C	527 °F	ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+15 ohm-cm	2.00e+15 ohm-cm	ASTM D257
	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	4.3 @Frequency 1e+6 Hz	4.3 @Frequency 1e+6 Hz	ASTM D150
	4.5 @Frequency 100 Hz	4.5 @Frequency 100 Hz	ASTM D150
Dissipation Factor	0.0050 @Frequency 100 Hz	0.0050 @Frequency 100 Hz	ASTM D150
	0.017 @Frequency 1e+6 Hz	0.017 @Frequency 1e+6 Hz	ASTM D150
High Voltage Arc Resistance to Ignition (HVAR)	150 sec	150 sec	ASTM D495
Comparative Tracking Index	550 V	550 V	ASTM D3638

Users viewing this material also viewed the following: