Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material was tested using the aggressive automotive coolant system, ethylene glycol with organic acid stabilizer, at 130°C (266°F). It exceeds the performance required by the automotive industry for polymeric materials exposed to high-temperature antifreeze solutions.Features: Antifreeze Resistant; Glycol Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Strength; LubricatedUses: Automotive Applications; Automotive Under the Hood; Housings; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Retention of Flexural Modulus - ISO 178 (130°C): 76 %; Retention of Flexural Strength - ISO 178 (130°C): 71 %; Retention of Tensile Modulus - ISO 527-2 (130°C): 75 %; Retention of Tensile Strength - ISO 527-2 (130°C): 69 %Automotive Specifications ASTM D6779 PA131G35 Color: BK328 Black; CHRYSLER MS-DB-478 CPN4771 Color: BK328 Black; GM GMP.PPA.019 Color: BK328 Black; GM GMW16360P-PPA-GF35 Color: BK328 Black; ISO 1874-PA6T/6I, MH, 11-120, GF33 Color: BK-328 Black; ISO 1874-PA6T/6I, MH, 11-120, GF33 Color: NT-07 NaturalInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4
0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4
0.010 cm/cm
0.010 in/in
Type D2; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 195 MPa
28300 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527-2
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 10.3 GPa
1490 ksi
ISO 178
Izod Impact, Notched (ISO) 8.10 kJ/m²
3.85 ft-lb/in²
Type 1, Notch A; ISO 180
Charpy Impact, Notched 0.820 J/cm²
3.90 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Melting Point 323 °C
613 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 295 °C
563 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 313 - 330 °C
595 - 626 °F
Front Barrel Temperature 326 - 339 °C
619 - 642 °F
Melt Temperature 331 - 352 °C
628 - 666 °F
Mold Temperature 150 °C
302 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Lubricant
Mold Release
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant