Solvay Specialty Polymers Amodel® AFA-4133 V0 Z Polyphthalamide (PPA), Dry (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AFA-4133 V0 Z Polyphthalamide (PPA), Dry (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AFA-4133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry. This resin has been shown to perform exceptionally well under soldering conditions that often cause blistering in many competitive resins. Its rapid crystallization rate can result in shorter cycles, thereby enhancing molding productivity and lowering costs. - Black: AFA-4133 V0 Z BK 324Injection Notes: Injection Rate: 3 to 4 in/sec Adjust holding pressure to 1/2 injection pressure. Set hold time to maximize part weight. A general purpose screw is recommended, with minimum back pressure.

Physical Properties	Metric	English	Comments
Specific Gravity	1.68 g/cc	1.68 g/cc	ASTM D792
Filler Content	33 %	33 %	Glass Fiber
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	165 MPa	23900 psi	ASTM D638
Elongation at Break	1.6 %	1.6 %	ASTM D638
Flexural Strength	221 MPa	32100 psi	ASTM D790
Flexural Modulus	13.1 GPa	1900 ksi	ASTM D790
Izod Impact, Notched	0.854 J/cm	1.60 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	325 °C	617 °F
Deflection Temperature at 1.8 MPa (264 psi)	295 °C	563 °F	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 0.794 mm	V-0 @Thickness 0.0313 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	ASTM D257
Dielectric Constant	4.2 @Frequency 1.00e+6 Hz	4.2 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	24.0 kV/mm @Thickness 1.59 mm	610 kV/in @Thickness 0.0626 in	ASTM D149
Dissipation Factor	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English	Comments
Feed Temperature	79.4 °C	175 °F	Hopper Temperature
Rear Barrel Temperature	316 - 324 °C	601 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	329 - 341 °C	624 - 646 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	121 °C @Time 14400 sec	250 °F @Time 4.00 hour
Moisture Content	0.15 %	0.15 %

Descriptive Properties	Value	Comments
Additive	Flame Retardant
Appearance	Black
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fast Molding Cycle
	Flame Retardant
	Good Chemical Resistance
	Good Dimensional Stability
	Good Electrical Properties
	Good Stiffness
	High Strength
	Hot Water Moldability
Forms	Pellets
Injection Rate	Fast
Processing Method	Water-Heated Mold Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Automotive Under the Hood
	Connectors
	Electrical Housing
	Electrical Parts
	Electrical/Electronic Applications
	General Purpose
	Housings
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement
	Power/Other Tools
	Valves/Valve Parts