Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded &nbs

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded &nbs.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL AFA-6133 V0 is a 33% glass-fiber reinforced grade of polyphthalamide (PPA) resin that was developed specifically for connector applications requiring compatibility with both "infrared" and "vapor phase" soldering operations typically used by the electronics industry. This resin processes readily using conventional injection molding equipment and methods. It offers high flow and short molding cycles. The processing window is relatively broad, and mold temperatures as low as 150°F (65°C) can be used.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
ASTM E831
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM E831
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 170 MPa
24700 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Flexural Yield Strength 224 MPa
32500 psi
ASTM D790
Flexural Modulus 13.2 GPa
1910 ksi
ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 4.1

@Frequency 1e+6 Hz
4.1

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm
610 kV/in
ASTM D149
Dissipation Factor 0.011

@Frequency 1e+6 Hz
0.011

@Frequency 1e+6 Hz
Processing Properties Metric English Comments
Melt Temperature 321 - 338 °C
610 - 640 °F
Injection