Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA), 45% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA), 45% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Electrical Properties; Good Stiffness; High Flow; High Strength; Hot Water MoldabilityUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Cell Phones; Connectors; Housings; Industrial Applications; Industrial PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA104G45Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183
Filler Content 45 %
45 %
Glass Fiber
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 193 MPa
28000 psi
ASTM D638
Elongation at Break 1.5 %
1.5 %
ASTM D638
Flexural Strength 276 MPa
40000 psi
ASTM D790
Flexural Modulus 15.5 GPa
2250 ksi
ASTM D790
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.794 mm
V-0

@Thickness 0.0313 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
4.1

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm

@Thickness 1.59 mm
584 kV/in

@Thickness 0.0626 in
ASTM D149
Dissipation Factor 0.011

@Frequency 1.00e+6 Hz
0.011

@Frequency 1.00e+6 Hz
ASTM D150
Comparative Tracking Index 400 - 600 V
400 - 600 V
PLC 1; UL 746
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 316 - 324 °C
601 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 321 - 338 °C
610 - 640 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Flame Retardant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Injection Rate Fast
Processing Technique Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant