Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded  (

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded  (.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offers excellent dimensional stability and chemical resistance, good mechanical properties and low warpage, and moisture absorption.This material is readily injection molded using conventional equipment and methods.Information provided by Solvay Advanced Polymers
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D792
1.49 g/cc
1.49 g/cc
ISO 1183A
Moisture Absorption at Equilibrium 0.20 %
0.20 %
24 hours; ASTM D570
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D785
Tensile Strength, Yield 81.0 MPa
11700 psi
ISO 527
85.0 MPa
12300 psi
ASTM D638
20.0 MPa

@Temperature 175 °C
2900 psi

@Temperature 347 °F
ISO 527
24.0 MPa

@Temperature 150 °C
3480 psi

@Temperature 302 °F
ISO 527
41.0 MPa

@Temperature 100 °C
5950 psi

@Temperature 212 °F
ISO 527
Elongation at Break 1.9 %
1.9 %
ISO 527
8.9 %

@Temperature 100 °C
8.9 %

@Temperature 212 °F
ISO 527
12.3 %

@Temperature 175 °C
12.3 %

@Temperature 347 °F
ISO 527
15 %

@Temperature 150 °C
15 %

@Temperature 302 °F
ISO 527
Elongation at Yield 2.1 %
2.1 %
ASTM D638
Tensile Modulus 5.80 GPa
841 ksi
ISO 527
6.10 GPa
885 ksi
ASTM D638
0.600 GPa

@Temperature 175 °C
87.0 ksi

@Temperature 347 °F
ISO 527
0.700 GPa

@Temperature 150 °C
102 ksi

@Temperature 302 °F
ISO 527
3.20 GPa

@Temperature 100 °C
464 ksi

@Temperature 212 °F
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
148 MPa
21500 psi
ASTM D790
15.0 MPa

@Temperature 175 °C
2180 psi

@Temperature 347 °F
ISO 178
18.0 MPa

@Temperature 150 °C
2610 psi

@Temperature 302 °F
ISO 178
60.0 MPa

@Temperature 100 °C
8700 psi

@Temperature 212 °F
ISO 178
Flexural Modulus 4.30 GPa
624 ksi
ISO 178
5.60 GPa
812 ksi
ASTM D790
0.600 GPa

@Temperature 175 °C
87.0 ksi

@Temperature 347 °F
ISO 178
0.700 GPa

@Temperature 150 °C
102 ksi

@Temperature 302 °F
ISO 178
3.30 GPa

@Temperature 100 °C
479 ksi

@Temperature 212 °F
ISO 178
Compressive Strength 162 MPa
23500 psi
ASTM D695
Poissons Ratio 0.32
0.32
Shear Modulus 2.20 - 2.31 GPa
319 - 335 ksi
Calculated
Shear Strength 74.0 MPa
10700 psi
ASTM D732
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.94 J/cm
13.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.90 kJ/m²
2.81 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²
25.2 ft-lb/in²
ISO 180/1U
Charpy Impact Unnotched 4.90 J/cm²
23.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.460 J/cm²
2.19 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 313 °C
595 °F
ASTM D3418
313 °C
595 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 154 °C
309 °F
ASTM D648
154 °C
309 °F
ISO 75Af