Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.125 in (3 mm). Key properties of this structural resin are high heat deflection temperature, high flexural modulus, high tensile strength, excellent creep resistance and low moisture absorption. - Black: AS-1133 HS BK 324 - Natural: AS-1133 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ISO 1183/B
Filler Content 33 %
33 %
Glass Fiber Reinforcement
Water Absorption 0.21 %

@Time 86400 sec
0.21 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.00 cm/cm
0.00 in/in
Conditioned; ASTM D955
0.0040 cm/cm
0.0040 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Conditioned; ASTM D955
0.0080 cm/cm
0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
R-Scale; ASTM D785
Tensile Strength at Break 193 MPa
28000 psi
Conditioned; ASTM D638
221 MPa
32100 psi
ASTM D638
Tensile Strength, Yield 225 MPa
32600 psi
ISO 527-2
Elongation at Break 2.1 %
2.1 %
Conditioned; ASTM D638
2.5 %
2.5 %
ASTM D638
3.0 %
3.0 %
ISO 527-2
Tensile Modulus 12.2 GPa
1770 ksi
ISO 527-2
13.1 GPa
1900 ksi
Conditioned; ASTM D638
13.1 GPa
1900 ksi
ASTM D638
Flexural Strength 326 MPa
47300 psi
ISO 178
Flexural Yield Strength 254 MPa
36800 psi
Conditioned; ASTM D790
317 MPa
46000 psi
ASTM D790
Flexural Modulus 10.3 GPa
1490 ksi
Conditioned; ASTM D790
10.3 GPa
1490 ksi
ASTM D790
10.3 GPa
1490 ksi
ISO 178
Compressive Strength 247 MPa
35800 psi
Conditioned; ASTM D695
276 MPa
40000 psi
ASTM D695
Poissons Ratio 0.41
0.41
ASTM E132
Shear Modulus 4.33 - 4.65 GPa
628 - 674 ksi
Calculated
Shear Strength 88.9 MPa
12900 psi
Conditioned; ASTM D732
101 MPa
14600 psi
ASTM D732
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
Conditioned; ASTM D256
0.850 J/cm
1.59 ft-lb/in
ASTM D256
10.0 J/cm
18.7 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 8.20 J/cm²
39.0 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C

@Temperature 160 - 249 °C
7.78 µin/in-°F

@Temperature 320 - 480 °F
TMA; ASTM E831
23.0 µm/m-°C

@Temperature 0.000 - 100 °C
12.8 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 59.0 µm/m-°C

@Temperature 0.000 - 100 °C
32.8 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
130 µm/m-°C

@Temperature 160 - 249 °C
72.2 µin/in-°F

@Temperature 320 - 480 °F
ASTM E831
Melting Point 310 °C
590 °F
Peak; ASTM D3418
310 °C
590 °F
ISO 11357-3
Maximum Service Temperature, Air 164 °C

@Time 7.20e+7 sec
327 °F

@Time 20000 hour
Continuous; ASTM D3045
185 °C

@Time 1.80e+7 sec
365 °F

@Time 5000 hour
Continuous; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.18 mm
567 °F

@Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Annealed; ISO 75-2/Af
285 °C

@Thickness 3.18 mm
545 °F

@Thickness 0.125 in
Annealed; ASTM D648
Flammability, UL94 HB

@Thickness 3.18 mm
HB

@Thickness 0.125 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
Conditioned; ASTM D257
1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 4.2

@Frequency 1.00e+6 Hz
4.2

@Frequency 1.00e+6 Hz
ASTM D150
4.3

@Frequency 1.00e+6 Hz
4.3

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
4.4

@Frequency 60.0 Hz
4.4

@Frequency 60.0 Hz
ASTM D150
4.7

@Frequency 60.0 Hz
4.7

@Frequency 60.0 Hz
Conditioned; ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 3.18 mm
533 kV/in

@Thickness 0.125 in
Conditioned; ASTM D149
21.0 kV/mm

@Thickness 3.18 mm
533 kV/in

@Thickness 0.125 in
ASTM D149
Dissipation Factor 0.0050

@Frequency 60.0 Hz
0.0050

@Frequency 60.0 Hz
ASTM D150
0.0090

@Frequency 60.0 Hz
0.0090

@Frequency 60.0 Hz
Conditioned; ASTM D150
0.017

@Frequency 1.00e+6 Hz
0.017

@Frequency 1.00e+6 Hz
ASTM D150
0.022

@Frequency 1.00e+6 Hz
0.022

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
Arc Resistance 120 sec
120 sec
Conditioned; ASTM D495
140 sec
140 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
UL 746
550 V
550 V
Conditioned; UL 746
Processing Properties Metric English Comments
Feed Temperature 79.4 °C
175 °F
Hopper Temperature
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Natural Color
Automotive Specifications ASTM D4000 PA121 G35 Color: BK324 Black
ASTM D4000 PA121 G35 Color: NT Natural
ASTM D4000 PPA0111 G33 GB145 KD200 KN090 PN080 YI265 Color: BK324 Black
ASTM D4000 PPA0111 G33 GB145 KD200 KN090 PN080 YI265 Color: NT Natural