- Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**)
Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications include electrical and electronic components. - Black: AS-4133 L BK 324 - Natural: AS-4133 L NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183/A |
| Filler Content | 33 % | 33 % | Glass Fiber Reinforcement |
| Water Absorption | 0.29 % @Temperature 23.0 °C, Time 86400 sec |
0.29 % @Temperature 73.4 °F, Time 24.0 hour |
0.29% typical, maximum 1.07%; ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | Conditioned; ASTM D638 |
| 200 MPa | 29000 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | Conditioned; ASTM D638 |
| 2.5 % | 2.5 % | ASTM D638 | |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Conditioned; ASTM D638 |
| 11.7 GPa | 1700 ksi | ASTM D638 | |
| Flexural Yield Strength | 241 MPa | 35000 psi | Conditioned; ASTM D790 |
| 290 MPa | 42100 psi | ASTM D790 | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | Conditioned; ASTM D790 |
| 11.0 GPa | 1600 ksi | ASTM D790 | |
| Compressive Strength | 172 MPa | 24900 psi | Conditioned; ASTM D695 |
| 179 MPa | 26000 psi | ASTM D695 | |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Modulus | 4.15 GPa | 602 ksi | Calculated |
| Shear Strength | 75.8 MPa | 11000 psi | Conditioned; ASTM D732 |
| 90.0 MPa | 13100 psi | ASTM D732 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | Conditioned; ASTM D256 |
| 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 | |
| 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature 149 - 249 °C |
7.78 µin/in-°F @Temperature 300 - 480 °F |
TMA; ASTM E831 |
| 22.0 µm/m-°C @Temperature 0.000 - 90.0 °C |
12.2 µin/in-°F @Temperature 32.0 - 194 °F |
TMA; ASTM E831 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature 0.000 - 90.0 °C |
32.8 µin/in-°F @Temperature 32.0 - 194 °F |
ASTM E831 |
| 120 µm/m-°C @Temperature 149 - 249 °C |
66.7 µin/in-°F @Temperature 300 - 480 °F |
ASTM E831 | |
| Melting Point | 327 °C | 621 °F | DSC |
| 327 °C | 621 °F | ASTM D570 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 320 °C @Thickness 3.18 mm |
608 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 300 °C @Thickness 3.18 mm |
572 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Conditioned; UL 746 |
| 600 V | 600 V | UL 746 | |
| High Voltage Arc-Tracking Rate, HVTR | 14.0 mm/min | 0.551 in/min | UL 746 |
| 18.0 mm/min | 0.709 in/min | Conditioned; UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 318 - 324 °C | 604 - 615 °F | |
| Front Barrel Temperature | 327 - 332 °C | 621 - 630 °F | |
| Melt Temperature | 329 - 343 °C | 624 - 649 °F | |
| Drying Temperature | 120 - 135 °C | 248 - 275 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | 0.045 % | 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Lubricant | |
| Appearance | Black | |
| Natural Color | ||
| Automotive Specifications | ASTM D6779 PA105G35 | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Fast Molding Cycle | |
| Good Chemical Resistance | ||
| Good Creep Resistance | ||
| Good Dimensional Stability | ||
| Good Stiffness | ||
| High Strength | ||
| Hot Water Moldability | ||
| Low Moisture Absorption | ||
| Lubricated | ||
| Forms | Pellets | |
| Generic | PPA | |
| Processing Method | Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| Uses | Automotive Applications | |
| Automotive Electronics | ||
| Automotive Under the Hood | ||
| Cell Phones | ||
| Electrical/Electronic Applications | ||
| General Purpose | ||
| Housings | ||
| Industrial Applications | ||
| Machine/Mechanical Parts | ||
| Metal Replacement | ||
| Power/Other Tools | ||
| Thick-walled Parts | ||
| Valves/Valve Parts |