Solvay Specialty Polymers Amodel® FC-1150 Polyphthalamide (PPA), 50% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® FC-1150 Polyphthalamide (PPA), 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® FC-1150 is an FDA-approved, 50% glass fiber reinforced resin designed for high strength and stiffness. This combines with its excellent thermal properties, low water absorption and good hydrolytic stability to make it particularly suited for components used in food service and consumer applications such coffee machines and ovens.Features: Chlorine Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Appliances; Consumer Applications; Filters; Housings; Industrial Applications; Plumbing Parts; Pump Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Flexural Strain - ISO 178 (23°C): 2.40Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Linear Mold Shrinkage, Flow 0.0014 - 0.0016 cm/cm

@Thickness 1.00 mm
0.0014 - 0.0016 in/in

@Thickness 0.0394 in
0.0015 - 0.0018 cm/cm

@Thickness 2.00 mm
0.0015 - 0.0018 in/in

@Thickness 0.0787 in
Linear Mold Shrinkage, Transverse 0.0042 - 0.0043 cm/cm

@Thickness 2.00 mm
0.0042 - 0.0043 in/in

@Thickness 0.0787 in
ASTM D955
0.0042 - 0.0046 cm/cm

@Thickness 1.00 mm
0.0042 - 0.0046 in/in

@Thickness 0.0394 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 270 MPa
39200 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
ISO 527-2
Tensile Modulus 19.1 GPa
2770 ksi
ISO 527-2
Flexural Strength 400 MPa
58000 psi
ISO 178
Flexural Modulus 18.4 GPa
2670 ksi
ISO 178
Charpy Impact Unnotched 8.80 J/cm²
41.9 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 300 °C
572 °F
Unannealed; Flatwise; ISO 75-2/A
Compliance Properties Metric English Comments
FDA Yes
Yes
Processing Properties Metric English Comments
Rear Barrel Temperature 315 - 330 °C
599 - 626 °F
Middle Barrel Temperature 320 - 340 °C
608 - 644 °F
Front Barrel Temperature 325 - 345 °C
617 - 653 °F
Melt Temperature 340 - 360 °C
644 - 680 °F
Mold Temperature 160 °C
320 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Suggested Max
Descriptive Properties Value Comments
Agency Ratings EU 10/2011; FDA 21 CFR 176.170(c)
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant