Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name AvaSpire®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire® AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire® AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin retains most of the desirable ultra-performance attributes of glass reinforced PEEK, including chemical resistance, fatigue resistance and long term thermal oxidative stability, but the heat deflection temperature is lower than 30% GF PEEK.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Industrial Applications; Medical Devices; Medical/Healthcare ApplicationsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ASTM D792
Filler Content 30 %
30 %
Glass Fiber
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ISO 62
Viscosity 650000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
650000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.18 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Thickness 3.18 mm
0.0090 - 0.011 in/in

@Thickness 0.125 in
ASTM D955
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 101
101
ASTM D785
Tensile Strength 147 MPa
21300 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 158 MPa
22900 psi
5 mm/min, Type 1A; ISO 527-2
Elongation at Break 3.2 %
3.2 %
Type 1A, 5 mm/min; ISO 527-2
3.2 %
3.2 %
5 mm/min; ASTM D638
Tensile Modulus 9.90 GPa
1440 ksi
5 mm/min; ASTM D638
10.6 GPa
1540 ksi
ISO 527-2
Flexural Strength 236 MPa
34200 psi
ISO 178
237 MPa
34400 psi
ASTM D790
Flexural Modulus 9.40 GPa
1360 ksi
ASTM D790
9.80 GPa
1420 ksi
ISO 178
Compressive Strength 159 MPa
23100 psi
ASTM D695
Poissons Ratio 0.43
0.43
ASTM E132
Shear Strength 84.5 MPa
12300 psi
ASTM D732
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.0 J/cm
18.7 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
9.44 µin/in-°F

@Temperature -58.0 - 122 °F
1
Specific Heat Capacity 1.29 J/g-°C

@Temperature 50.0 °C
0.308 BTU/lb-°F

@Temperature 122 °F
ASTM C351
1.66 J/g-°C

@Temperature 200 °C
0.397 BTU/lb-°F

@Temperature 392 °F
ASTM C351
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 340 °C
644 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 217 °C
423 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
DSC
Flammability, UL94 V-1

@Thickness 0.800 mm
V-1

@Thickness 0.0315 in
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 2.10e+17 ohm-cm
2.10e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.48

@Frequency 1.00e+6 Hz
3.48

@Frequency 1.00e+6 Hz
ASTM D150
3.52

@Frequency 60.0 Hz
3.52

@Frequency 60.0 Hz
ASTM D150
3.53

@Frequency 1000 Hz
3.53

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 15.0 kV/mm

@Thickness 3.00 mm
381 kV/in

@Thickness 0.118 in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
ASTM D150
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 366 - 388 °C
691 - 730 °F
Mold Temperature 149 - 177 °C
300 - 351 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Beige; Black
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding; Machining; Profile Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0