Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 microns) can be successfully melt extruded out of AV-630 using conventional thermoplastics film extrusion equipment. Films of AV-630 offer certain performance advantages over comparable PEEK film. These include improved toughness and ductility, a higher retention of mechanical integrity at temperatures above 150°C, better acceptance of adhesives and improved flame propagation resistance properties. Ultra-thin films (
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ASTM D570
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
M-Scale; ASTM D785
Tensile Strength 92.0 MPa
13300 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 89.0 MPa
12900 psi
ISO 527-2/1A/50
Elongation at Break 50 - 80 %
50 - 80 %
50 mm/min; ASTM D638
50 - 80 %
50 - 80 %
ISO 527-2/1A/50
Elongation at Yield 5.4 %
5.4 %
ISO 527-2/1A/50
6.0 %
6.0 %
50 mm/min; ASTM D638
Tensile Modulus 3.30 GPa
479 ksi
50 mm/min; ASTM D638
3.40 GPa
493 ksi
ISO 527-2/1A/1
Flexural Strength 127 MPa
18400 psi
ASTM D790
128 MPa
18600 psi
ISO 178
Flexural Modulus 0.320 GPa
46.4 ksi
ASTM D790
3.30 GPa
479 ksi
ISO 178
Compressive Strength 110 MPa
16000 psi
ASTM D695
Shear Strength 79.0 MPa
11500 psi
ASTM D732
Izod Impact, Notched 0.910 J/cm
1.70 ft-lb/in
ASTM D256
NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
Specific Heat Capacity 1.39 J/g-°C

@Temperature 50.0 °C
0.332 BTU/lb-°F

@Temperature 122 °F
DSC
1.96 J/g-°C

@Temperature 200 °C
0.468 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 340 °C
644 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
Annealed; 2 hours at 200°C; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
ASTM D3418
Oxygen Index 38 %
38 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 6.20e+17 ohm-cm
6.20e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Strength 180 kV/mm

@Thickness 0.0600 mm
4570 kV/in

@Thickness 0.00236 in
Amorphous Film; ASTM D149
Processing Properties Metric English Comments
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Natural Color
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Impact Resistance
High Heat Resistance
Forms Pellets
Generic PAEK
Processing Method Extrusion Blow Molding
Fiber (Spinning) Extrusion
Film Extrusion
Injection Blow Molding
Injection Molding
Machining
Profile Extrusion
Thermoforming
Wire & Cable Extrusion
Uses Aerospace Applications
Aircraft Applications
Electronic Insulation
Film
Laminates
Liners