Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 microns) can be successfully melt extruded out of AV-630 using conventional thermoplastics film extrusion equipment.Films of AV-630 offer certain performance advantages over comparable PEEK film. These include improved toughness and ductility, a higher retention of mechanical integrity at temperatures above 150°C, better acceptance of adhesives and improved flame propagation resistance properties. Ultra-thin films (
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 92 | 92 | ASTM D785 |
| Tensile Strength | 92.0 MPa | 13300 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type 1A, 50 mm/min; ISO 527-2 |
| Elongation at Break | 50 - 80 % | 50 - 80 % | Type 1A, 50 mm/min; ISO 527-2 |
| 50 - 80 % | 50 - 80 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.4 % | 5.4 % | Type 1A, 50 mm/min; ISO 527-2 |
| 6.0 % | 6.0 % | 50 mm/min; ASTM D638 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 50 mm/min; ASTM D638 |
| 3.40 GPa | 493 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 127 MPa | 18400 psi | ASTM D790 |
| 128 MPa | 18600 psi | ISO 178 | |
| Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
| 3.30 GPa | 479 ksi | ISO 178 | |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Shear Strength | 79.0 MPa | 11500 psi | ASTM D732 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.39 J/g-°C @Temperature 50.0 °C |
0.332 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.96 J/g-°C @Temperature 200 °C |
0.468 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C @Thickness 3.20 mm |
358 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Oxygen Index | 38 % | 38 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.20e+17 ohm-cm | 6.20e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Strength | 180 kV/mm @Thickness 0.0600 mm |
4570 kV/in @Thickness 0.00236 in |
Amorphous Film; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Natural | |
| Form | Pellets | |
| Processing Technique | Extrusion Blow Molding | |
| Fiber (Spinning) Extrusion; Film Extrusion | ||
| Injection Blow Molding; Injection Molding | ||
| Machining; Profile Extrusion | ||
| Thermoforming; Wire & Cable Extrusion |