Solvay Specialty Polymers Halar® 500 ECTFE Fluoropolymer (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Halar® 500 ECTFE Fluoropolymer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer.HALAR® Fluoropolymers have excellent barrier properties, high resistance to a variety of corrosive chemicals and solvents, low flammability, and ease of processing.

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0607 lb/in³
Water Absorption	<= 0.10 %	<= 0.10 %	168 hours
Moisture Absorption at Equilibrium	<= 0.10 %	<= 0.10 %	after 168 hours

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	90	90
Hardness, Shore D	75	75
Tensile Strength, Ultimate	46.0 MPa	6670 psi
Tensile Strength, Yield	29.0 MPa	4210 psi
Elongation at Break	260 %	260 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	1.655 GPa	240.0 ksi
Flexural Yield Strength	47.0 MPa	6820 psi
Flexural Modulus	1.69 GPa	245 ksi
Izod Impact, Notched	0.640 J/cm @Temperature -40.0 °C	1.20 ft-lb/in @Temperature -40.0 °F
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F
Tensile Impact Strength	806 kJ/m²	384 ft-lb/in²	ASTM D1822S
Coefficient of Friction, Dynamic	0.19	0.19	vs. steel; 50 cm/s (20 in/s); ASTM D1044
Coefficient of Friction, Static	0.19	0.19	vs. steel; ASTM D1044
Taber Abrasion, mg/1000 Cycles	5.0	5.0	CS-17 wheels; 500 g; wheels cleaned every 25 cycles

Thermal Properties	Metric	English	Comments
CTE, linear	80.0 µm/m-°C @Temperature -30.0 - 50.0 °C	44.4 µin/in-°F @Temperature -22.0 - 122 °F
	135 µm/m-°C @Temperature 85.0 - 125 °C	75.0 µin/in-°F @Temperature 185 - 257 °F
Specific Heat Capacity	0.946 J/g-°C	0.226 BTU/lb-°F
Thermal Conductivity	0.151 W/m-K	1.05 BTU-in/hr-ft²-°F	Halar® 300
Melting Point	240 °C	464 °F
Maximum Service Temperature, Air	140 °C	284 °F
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F
Deflection Temperature at 1.8 MPa (264 psi)	67.0 °C	153 °F
Brittleness Temperature	<= -76.0 °C	<= -105 °F
Flammability, UL94	V-0 @Thickness 0.180 mm	V-0 @Thickness 0.00709 in
Oxygen Index	>= 52 %	>= 52 %

Optical Properties	Metric	English	Comments
Refractive Index	1.4476 @Wavelength 589 nm	1.4476 @Wavelength 589 nm
Haze	3.0 - 5.0 %	3.0 - 5.0 %	typical for HALAR films; ASTM D1003
Gloss	85 - 95 %	85 - 95 %	85-95% at 20° is typical of HALAR films; ASTM D2457

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.56e+16 ohm-cm	1.56e+16 ohm-cm
Surface Resistance	>= 1.00e+17 ohm	>= 1.00e+17 ohm	ASTM D257
Dielectric Constant	2.47 @Frequency 1000 Hz	2.47 @Frequency 1000 Hz
	2.57 @Frequency 1e+6 Hz	2.57 @Frequency 1e+6 Hz
Dielectric Strength	14.0 kV/mm @Thickness 1.60 mm	356 kV/in @Thickness 0.0630 in
	14.0 kV/mm @Thickness 3.18 mm	356 kV/in @Thickness 0.125 in
	80.0 kV/mm @Thickness 0.0250 mm	2030 kV/in @Thickness 0.000984 in
Dissipation Factor	0.0014 @Frequency 1000 Hz	0.0014 @Frequency 1000 Hz
	0.013 @Frequency 1e+6 Hz	0.013 @Frequency 1e+6 Hz
Arc Resistance	>= 50 sec	>= 50 sec	Test Terminated at 50 sec.; ASTM D495
Comparative Tracking Index	>= 600 V @Thickness 1.60 mm	>= 600 V @Thickness 0.0630 in
Hot Wire Ignition, HWI	20.2 sec @Thickness 1.60 mm	20.2 sec @Thickness 0.0630 in
High Amp Arc Ignition, HAI	>= 200 arcs @Thickness 1.60 mm	>= 200 arcs @Thickness 0.0630 in	test terminated at 200 arcs 1/16 A.S.
High Voltage Arc-Tracking Rate, HVTR	208 mm/min @Thickness 1.60 mm	8.19 in/min @Thickness 0.0630 in

Processing Properties	Metric	English	Comments
Processing Temperature	260 - 282 °C	500 - 540 °F