Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA), 50% Glass Fiber (Dry)

Category Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA), 50% Glass Fiber (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; High Stiffness; High Strength; Impact Modified; Low Moisture Absorption; Outstanding Surface FinishUses: Appliance Components; Appliances; Automotive Applications; Automotive Electronics; Business Equipment; Camera Applications; Electrical Housing; Electrical/Electronic Applications; Furniture; Gears; Housings; Industrial Applications; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ISO 62
Water Absorption at Saturation 1.5 %
1.5 %
65% RH; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 235 MPa
34100 psi
ISO 527-2
Elongation at Break 2.6 %
2.6 %
ISO 527-2
Tensile Modulus 17.0 GPa
2470 ksi
ISO 527-2
Flexural Strength 360 MPa
52200 psi
ISO 178
Flexural Modulus 17.0 GPa
2470 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
Izod Impact, Unnotched 11.0 J/cm
20.6 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Annealed; ISO 75-2/A
Flammability, UL94 HB

@Thickness >=0.600 mm
HB

@Thickness >=0.0236 in
Oxygen Index 25 %
25 %
ISO 4589-2
Electrical Properties Metric English Comments
Dielectric Constant 4.23

@Frequency 1.00e+9 Hz
4.23

@Frequency 1.00e+9 Hz
ASTM D2520
4.27

@Frequency 2.40e+9 Hz
4.27

@Frequency 2.40e+9 Hz
ASTM D2520
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243-1
Dissipation Factor 0.0095
0.0095
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 280 °C
500 - 536 °F
Melt Temperature 270 °C
518 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C

@Time 1800 - 5400 sec
248 °F

@Time 0.500 - 1.50 hour
Descriptive Properties Value Comments
Additive Impact Modifier
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Colors; Natural
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant