Solvay Specialty Polymers Ixef® 2057 Polyarylamide (PARA), 45% Mineral Filler  (discontinued **)

Category Polymer , Thermoplastic , Polyamide-imide (PAI)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2057 Polyarylamide (PARA), 45% Mineral Filler  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 2057 is a 45% mineral-reinforced polyarylamide which exhibits high strength and stiffness, and outstanding surface gloss. Due to its mineral reinforcement, Ixef 2057 resin mold with very low warpage.- Black: Ixef 2057/9000- Custom ColorableFeatures: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Strength; High Flow; High Stiffness; Low Moisture Absorption; Low Warpage; Outstanding Surface FinishUses: Appliance Components; Appliances; Automotive Applications; Automotive Under the Hood; Bushings; Business Equipment; Furniture; Gears; Industrial Applications; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsAvailability: Africa & Middle East; Asia Pacific; Europe; North America; South AmericaHot Runners: 250°C to 260°C (482°F to 500°F)Injection Pressure" rapidDryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIXEF 2057 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260°C to 290°C (500°F to 554°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position.Information provide by Solvay Specialty Polymers
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ISO 1183
Water Absorption 0.18 %
0.18 %
24 hrs; ISO 62
Linear Mold Shrinkage 0.0040 - 0.0050 cm/cm
0.0040 - 0.0050 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-2
Elongation at Break 1.6 %
1.6 %
ISO 527-2
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-2
Flexural Strength 170 MPa
24700 psi
ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
ISO 178
Izod Impact, Notched 0.350 J/cm
0.656 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.00 J/cm
5.62 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C
7.78 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Descriptive Properties Value Comments
Additional Properties Moisture Absorption - Internal Method: 1.8 %
Appearance Black; Colors Available
Forms Pellets
Processing Method Injection Molding
RoHS Compliance RoHS Compliant