Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, at Equilibrium (65% RH)  (discontin

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, at Equilibrium (65% RH)  (discontin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
DAM; ISO 1183
Filler Content 30 %
30 %
Carbon
Water Absorption 0.22 %
0.22 %
24 hr (DAM); ISO 62
Moisture Absorption at Equilibrium 2.0 %
2.0 %
65% RH (beginning DAM); Solvay Test
Linear Mold Shrinkage, Flow 0.00050 - 0.0015 cm/cm
0.00050 - 0.0015 in/in
Solvay Test
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ISO 527
Elongation at Break 1.3 %
1.3 %
ISO 527
Tensile Modulus 23.0 GPa
3340 ksi
ISO 527
Flexural Strength 270 MPa
39200 psi
ISO 178
Flexural Modulus 21.0 GPa
3050 ksi
ISO 178
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ISO 180
Izod Impact, Unnotched 3.45 J/cm
6.46 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
Processing Properties Metric English Comments
Feed Temperature 250 - 280 °C
482 - 536 °F
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Compression Zone
Middle Barrel Temperature 250 - 280 °C
482 - 536 °F
Homogenization Zone
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Zone
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Needed to develop high crystallinity
Injection Pressure 50.0 - 250 MPa
7250 - 36300 psi
Hold Pressure 30.0 - 150 MPa
4350 - 21800 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi