Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)

Category Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA), 50% Glass Fiber (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® GS-1022 is a 50% glass-fiber reinforced grade of polyarylamide (PARA) available in several colors. Parts molded from these colored resins can withstand high-energy gamma radiation without significant change in appearance and physical properties. Ixef® GS-1022 resins demonstrate no evidence of cytotoxicity, sensitization, intracutaneous reactivity or acute systemic toxicity, based on biocompatibility testing as defined by ISO 10993-1.Features: Biocompatible; E-beam Sterilizable; Ethylene Oxide Sterilizable; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Sterilizability; High Flow; High Strength; Low Moisture Absorption; Outstanding Surface Finish; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Ultra High StiffnessUses: Dental Applications; Hospital Goods; Medical Devices; Medical/Healthcare Applications; Surgical InstrumentsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Additional Properties: Moisture Absorption - Internal Method 1.5 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Water Absorption 0.16 %

@Time 86400 sec
0.16 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 265 MPa
38400 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 22.0 GPa
3190 ksi
ISO 527-2
Flexural Strength 380 MPa
55100 psi
ISO 178
Flexural Modulus 22.0 GPa
3190 ksi
ISO 178
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
8.33 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C

@Time 1800 - 5400 sec
248 °F

@Time 0.500 - 1.50 hour
Descriptive Properties Value Comments
Additive Gamma Stabilizer
Agency Ratings ISO 10993
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Colors Available
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding