Solvay Specialty Polymers Kalix® 2855 Polyamide, High Performance (HPPA), Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Kalix®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Kalix® 2855 Polyamide, High Performance (HPPA), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kalix® 2855 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is formulated to provide maximum strength, stiffness, impact resistance, and post-mold dimensional stability in thermoplastic parts. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry.Features: Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; Low Moisture Absorption; Low Warpage; Paintable; PlatableUses: Cell Phones; Electrical Parts; Electrical/Electronic Applications; Thin-walled PartsInjection Molding Notes: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding.Additional Properties: Biobased Content - ASTM D6866 27 %; Flexural Elongation at Break - 3.9 %; Specific Gravity - 1.55Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Water Absorption 0.090 %

@Time 86400 sec
0.090 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0015 cm/cm
0.0015 in/in
Linear Mold Shrinkage, Transverse 0.0058 cm/cm
0.0058 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 230 MPa
33400 psi
ISO 527-2
Elongation at Break 3.8 %
3.8 %
ISO 527-2
Tensile Modulus 19.0 GPa
2760 ksi
ISO 527-2
Flexural Strength 355 MPa
51500 psi
ISO 178
Flexural Modulus 17.0 GPa
2470 ksi
ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 95.0 kJ/m²
45.2 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
HDT B; Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
Unannealed; ISO 75-2/A
Glass Transition Temp, Tg 40.0 °C
104 °F
DSC
Electrical Properties Metric English Comments
Dielectric Constant 3.77

@Frequency 2.40e+9 Hz
3.77

@Frequency 2.40e+9 Hz
ASTM D2520
Dissipation Factor 0.013

@Frequency 2.40e+9 Hz
0.013

@Frequency 2.40e+9 Hz
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 280 - 295 °C
536 - 563 °F
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content <= 0.090 %
<= 0.090 %
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
North America
Color Black; White
Form Pellets
Part Marking Code >PA610-GF55<
ISO 11469
Processing Technique Injection Molding; Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant