Solvay Specialty Polymers Kalix® 2955 Polyamide, High Performance (HPPA), Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Kalix®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Kalix® 2955 Polyamide, High Performance (HPPA), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kalix® 2955 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry.Features: Fast Molding Cycle; Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; Low Warpage; Paintable; PlatableUses: Cell Phones; Electrical Parts; Electrical/Electronic Applications; Thin-walled PartsInjection Molding Notes: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding.Additional Properties: Biobased Content - ASTM D6866 27 %; Flexural Strain at Break - ISO 178 3.0 %; Specific Gravity - 1.58Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Water Absorption 0.090 %

@Time 86400 sec
0.090 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0013 cm/cm
0.0013 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0033 cm/cm
0.0033 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Stress 222 MPa
32200 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
Tensile Modulus 17.8 GPa
2580 ksi
ISO 527-2
Flexural Strength 330 MPa
47900 psi
ISO 178
Flexural Modulus 15.8 GPa
2290 ksi
ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 87.0 kJ/m²
41.4 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
HDT B; Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
Unannealed; ISO 75-2/A
Glass Transition Temp, Tg 40.0 °C
104 °F
DSC
Flammability, UL94 HB

@Thickness >=0.600 mm
HB

@Thickness >=0.0236 in
Electrical Properties Metric English Comments
Dielectric Constant 4.13

@Frequency 1.00e+9 Hz
4.13

@Frequency 1.00e+9 Hz
ASTM D2520
Dissipation Factor 0.011

@Frequency 2.40e+9 Hz
0.011

@Frequency 2.40e+9 Hz
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 280 - 295 °C
536 - 563 °F
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C

@Time 14400 - 43200 sec
176 °F

@Time 4.00 - 12.0 hour
Moisture Content <= 0.090 %
<= 0.090 %
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
North America
Color Black; White
Form Pellets
Part Marking Code >PA610-GF55<
ISO 11469
Processing Technique Injection Molding; Water-Heated Mold Injection Molding