Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KetaSpire KT-850 is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color pellet form. KetaSpire PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. - Natural: KT-850 NTInjection Notes: Back Pressure: minimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Viscosity | 380000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
380000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.18 mm |
0.012 in/in @Thickness 0.125 in |
5" x 0.5" x 0.125" bar; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 3.18 mm |
0.014 in/in @Thickness 0.125 in |
5" x 0.5" x 0.125" bar; ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 400 °C |
10 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 @Time 1.00 sec |
88 @Time 0.000278 hour |
ASTM D2240 |
| Tensile Strength | 96.5 MPa | 14000 psi | 51 mm/min; ASTM D638 |
| Elongation at Break | 20 - 30 % | 20 - 30 % | 51 mm/min; ASTM D638 |
| >= 50 % | >= 50 % | 5.1 mm/min; ASTM D638 | |
| Elongation at Yield | 5.2 % | 5.2 % | 51 mm/min; ASTM D638 |
| Tensile Modulus | 3.65 GPa | 529 ksi | 51 mm/min; ASTM D638 |
| Flexural Strength | 146 MPa | 21200 psi | ASTM D790 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
23.9 µin/in-°F @Temperature -58.0 - 122 °F |
TMA; ASTM E831 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 355 °C | 671 °F | |
| Middle Barrel Temperature | 365 °C | 689 °F | |
| Front Barrel Temperature | 370 °C | 698 °F | |
| Nozzle Temperature | 375 °C | 707 °F | |
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Ductile | |
| Fatigue Resistant | ||
| Flame Retardant | ||
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| Good Impact Resistance | ||
| High Heat Resistance | ||
| Forms | Pellets | |
| Generic | PEEK | |
| Injection Rate | Fast | |
| Processing Method | Extrusion Blow Molding | |
| Film Extrusion | ||
| Injection Molding | ||
| Machining | ||
| Profile Extrusion | ||
| Thermoforming | ||
| Wire & Cable Extrusion | ||
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | |
| Uses | Aircraft Applications | |
| Automotive Applications | ||
| Bearings | ||
| Bushings | ||
| Compounding | ||
| Electrical/Electronic Applications | ||
| Film | ||
| Industrial Applications | ||
| Medical/Healthcare Applications | ||
| Oil/Gas Applications | ||
| Seals | ||
| Tubing |