Solvay Specialty Polymers Ryton® QA200N Polyphenylene Sulfide (PPS)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS); Molded
Manufacturer Solvay Specialty Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® QA200N Polyphenylene Sulfide (PPS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® QA200N (granular powder) unfilled polyphenylene sulfide exhibits excellent thermal stability and chemical resistance.Features: Good Chemical Resistance; Good Thermal StabilityAdditional Properties: Ash Content - ISO 3451-1 0.1 wt%; Volatiles - (150°C): < 0.3 wt%Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Water Absorption 0.050 %

@Time 86400 sec
0.050 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.010 cm/cm

@Thickness 3.18 mm
0.010 in/in

@Thickness 0.125 in
Melt Flow 100 g/10 min

@Load 5.00 kg,
Temperature 316 °C
100 g/10 min

@Load 11.0 lb,
Temperature 601 °F
Procedure B; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Stress 80.0 MPa
11600 psi
ISO 527-2
Elongation at Break 4.0 %
4.0 %
ISO 527-2
Tensile Modulus 3.40 GPa
493 ksi
ISO 527-2
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 3.40 GPa
493 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm

@Thickness 3.18 mm
0.993 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
Notch A; ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
27.8 µin/in-°F

@Temperature -58.0 - 122 °F
2
120 µm/m-°C

@Temperature 100 - 200 °C
66.7 µin/in-°F

@Temperature 212 - 392 °F
2
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 280 °C
536 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Unannealed; ASTM D648
Vicat Softening Point >= 180 °C
>= 356 °F
ISO 306
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-2
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 44 %
44 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm
610 kV/in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Natural
Form Powder
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant