Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Black Polyphenylene Sulfide CompoundRyton® R-4-220BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications requiring constant or repeated exposure to high temperature water. Retains 80% of its tensile strength and gains 1% in rate.Comments: Test specimen molding conditions: Stock Temperature, 315-345°C; Mold Temperature, 135°C; ASTM Values Converted to SI UnitsData provided by Chevron Phillips Chemical Company LP.Solvay Specialty Polymers has acquired the Ryton product line.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ASTM D792
Water Absorption 0.020 %
0.020 %
ASTM D570
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
102 mm X 102 mm X 3.2 mm Plaques, Edge Gated
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
Measured on 102 mm X 102 mm X 3.2 mm Plaques, Edge Gated
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 180 MPa
26100 psi
ISO 527
Elongation at Break 1.4 %
1.4 %
ISO 527
Flexural Yield Strength 240 MPa
34800 psi
ISO 178
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Compressive Yield Strength 235 MPa
34100 psi
ASTM D695
Izod Impact, Unnotched 3.00 J/cm
5.62 ft-lb/in
J/cm²; ISO 180A
Izod Impact Resistance 0.600 J/cm²
2.86 ft-lb/in²
ISO 180A
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature 100 - 200 °C
7.78 µin/in-°F

@Temperature 212 - 392 °F
Axial; ASTM E831
16.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
8.89 µin/in-°F

@Temperature -58.0 - 122 °F
Axial; ASTM E831
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ASTM E831
94.0 µm/m-°C

@Temperature 100 - 200 °C
52.2 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Maximum Service Temperature, Air 200 °C
392 °F
UL Temperature Index 200 / 220 per UL746B
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Annealed 2 hr @ 200°C; ASTM D653
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 5.00e+14 ohm-cm
5.00e+14 ohm-cm
ASTM D257
Surface Resistance 1.00e+12 ohm

@Temperature 90.0 °C
1.00e+12 ohm

@Temperature 194 °F
95% RH, 48 hrs
Dielectric Constant 4.0

@Frequency 1000 Hz
4.0

@Frequency 1000 Hz
ASTM D150
4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
ASTM D150
0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 125 sec
125 sec
ASTM D495
Comparative Tracking Index 150 V
150 V
UL 746A