Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional molding equipment.Features: Good Flow; Good StrengthInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.95 g/cc
0.0704 lb/in³
ASTM D792
Water Absorption 0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 3.18 mm
0.0020 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0040 cm/cm

@Thickness 3.20 mm
0.0040 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 101
101
ASTM D785
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength 131 MPa
19000 psi
ASTM D638
Tensile Stress 135 MPa
19600 psi
ISO 527-2
Elongation at Break 1.0 %
1.0 %
ISO 527-2
1.0 %
1.0 %
ASTM D638
Flexural Strength 207 MPa
30000 psi
ASTM D790
210 MPa
30500 psi
ISO 178
Flexural Modulus 17.2 GPa
2490 ksi
ASTM D790
18.0 GPa
2610 ksi
ISO 178
Compressive Strength 285 MPa
41300 psi
ASTM D695
Poissons Ratio 0.36
0.36
ASTM E132
Izod Impact, Notched 0.590 J/cm

@Thickness 3.18 mm
1.11 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 2.10 J/cm

@Thickness 3.18 mm
3.93 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
Notch A; ISO 180
Izod Impact, Unnotched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature 100 - 200 °C
8.33 µin/in-°F

@Temperature 212 - 392 °F
2
15.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
8.33 µin/in-°F

@Temperature -58.0 - 122 °F
2
CTE, linear, Transverse to Flow 30.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
16.7 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
70.0 µm/m-°C

@Temperature 100 - 200 °C
38.9 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
Thermal Conductivity 0.580 W/m-K
4.03 BTU-in/hr-ft²-°F
ASTM C177
Maximum Service Temperature, Air 220 - 240 °C
428 - 464 °F
UL Temperature Rating
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
Oxygen Index 61 %
61 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Insulation Resistance 1.00e+11 ohm

@Temperature 90.0 °C
1.00e+11 ohm

@Temperature 194 °F
IEC 60167
Dielectric Constant 4.8

@Frequency 1000 Hz
4.8

@Frequency 1000 Hz
ASTM D150
4.9

@Frequency 1.00e+6 Hz
4.9

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 18.0 kV/mm
457 kV/in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
0.0040

@Frequency 60.0 Hz
0.0040

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 185 sec
185 sec
ASTM D495
Comparative Tracking Index 250 V
250 V
UL 746
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Natural
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant