Solvay Specialty Polymers Ryton® XK2340 Polyphenylene Sulfide Alloy (PPS Alloy), 40% Glass Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Solvay Specialty Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® XK2340 Polyphenylene Sulfide Alloy (PPS Alloy), 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® XK2340 40% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength, toughness, and rigidity, along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. It may be easily molded in conventional injection molding equipment utilizing water heated molds.Features: Fast Molding Cycle; Good Flow; Good Strength; Good Toughness; High RigidityInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ASTM D792
Filler Content 40 %
40 %
Glass Fiber
Water Absorption 0.30 %

@Time 86400 sec
0.30 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 3.18 mm
0.0030 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Thickness 3.20 mm
0.0060 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength 193 MPa
28000 psi
ASTM D638
Tensile Stress 195 MPa
28300 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
1.8 %
1.8 %
ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
270 MPa
39200 psi
ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
ISO 178
12.4 GPa
1800 ksi
ASTM D790
Compressive Strength 255 MPa
37000 psi
ASTM D695
Poissons Ratio 0.42
0.42
ASTM E132
Izod Impact, Notched 0.850 J/cm

@Thickness 3.18 mm
1.59 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 6.40 J/cm

@Thickness 3.18 mm
12.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
Notch A; ISO 180
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature 100 - 200 °C
8.33 µin/in-°F

@Temperature 212 - 392 °F
2
20.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
11.1 µin/in-°F

@Temperature -58.0 - 122 °F
2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
30.6 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
100 µm/m-°C

@Temperature 100 - 200 °C
55.6 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Oxygen Index 35 %
35 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Insulation Resistance 1.00e+12 ohm

@Temperature 90.0 °C
1.00e+12 ohm

@Temperature 194 °F
IEC 60167
Dielectric Constant 3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
ASTM D150
4.3

@Frequency 1000 Hz
4.3

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 22.0 kV/mm
559 kV/in
ASTM D149
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM D150
0.020

@Frequency 1000 Hz
0.020

@Frequency 1000 Hz
ASTM D150
Arc Resistance 100 sec
100 sec
ASTM D495
Comparative Tracking Index 275 V
275 V
UL 746
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant