Solvay Specialty Polymers Torlon® 4203L Polyamide-imide (PAI)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Torlon® 4203L Polyamide-imide (PAI)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Torlon 4203L is an unreinforced, lubricated, pigmented grade of polyamide-imide (PAI) resin. It has the best impact resistance and greatest elongation of all the Torlon grades. Torlon PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. Torlon 4203L resin offers outstanding electrical properties, which makes it ideal for high performance parts such as connectors, switches and relays. In addition Torlon 4203L polyamide-imide can be used in applications such as thrust washers, spline liners, valve seats, bushings, bearings, wear rings, cams and other applications requiring strength at high temperature and resistance to wear. - High Flow: Torlon 4203L-HF - Low Flow: Torlon 4203L-LFInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Water Absorption 0.33 %

@Time 86400 sec
0.33 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.0085 cm/cm
0.0060 - 0.0085 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 152 MPa
22000 psi
Type I; ASTM D638
Tensile Stress 192 MPa
27800 psi
ASTM D1708
Elongation at Break 7.6 %
7.6 %
Type I; ASTM D638
15 %
15 %
ASTM D1708
Tensile Modulus 4.48 GPa
650 ksi
Type I; ASTM D638
4.90 GPa
711 ksi
ASTM D1708
Flexural Strength 118 MPa

@Temperature 232 °C
17100 psi

@Temperature 450 °F
ASTM D790
241 MPa

@Temperature 23.0 °C
35000 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 3.59 GPa

@Temperature 232 °C
521 ksi

@Temperature 450 °F
ASTM D790
5.03 GPa

@Temperature 23.0 °C
730 ksi

@Temperature 73.4 °F
ASTM D790
Compressive Strength 221 MPa
32100 psi
ASTM D695
Compressive Modulus 4.00 GPa
580 ksi
ASTM D695
Poissons Ratio 0.45
0.45
ASTM E132
Shear Modulus 1.54 - 1.69 GPa
223 - 245 ksi
Calculated
Izod Impact, Notched 1.40 J/cm
2.62 ft-lb/in
ASTM D256
11.0 J/cm
20.6 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 31.0 µm/m-°C
17.2 µin/in-°F
TMA; ASTM E831
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 278 °C
532 °F
Unannealed; ASTM D648
Glass Transition Temp, Tg 277 °C
531 °F
Tg, onset, Method is equivalent to ISO 11357-2.; DSC
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Surface Resistance 5.00e+18 ohm
5.00e+18 ohm
ASTM D257
Dielectric Constant 3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
ASTM D150
4.2

@Frequency 60.0 Hz
4.2

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm
584 kV/in
ASTM D149
Dissipation Factor 0.026

@Frequency 60.0 Hz
0.026

@Frequency 60.0 Hz
ASTM D150
0.031

@Frequency 1.00e+6 Hz
0.031

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 304 °C
579 °F
Nozzle Temperature 371 °C
700 °F
Mold Temperature 199 - 216 °C
390 - 421 °F
Drying Temperature 177 °C
351 °F
Dry Time 3.00 hour
3.00 hour
Moisture Content 0.050 %
0.050 %
Back Pressure 6.89 MPa
999 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Additive PTFE Lubricant
Automotive Specifications ASTM D4000 PAI000 R03 A56316 GA140 Z1Z2Z3Z4Z5Z6, Dwg YC3P-7E195-AA
CHRYSLER MS-DB405 CPN3373 Color: Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Creep Resistance
Good Electrical Properties
Good Wear Resistance
High Heat Resistance
High Temperature Strength
Low Temperature Toughness
Ultra High Impact Resistance
Forms Pellets
Generic PAI
Processing Method Injection Molding
Machining
Profile Extrusion
RoHS Compliance RoHS Compliant
Screw L/D Ratio 18.0:1.0 to 24.0:1.0
Uses Aircraft Applications
Automotive Applications
Bushings
Connectors
Electrical Parts
Electrical/Electronic Applications
Fasteners
Film
Machine/Mechanical Parts
Oil/Gas Applications
Semiconductor Molding Compounds
Thrust Washer