Solvay Specialty Polymers Udel® P-3700 HC Polysulfone (PSU)

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer Solvay Specialty Polymers
Trade Name Udel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Udel® P-3700 HC Polysulfone (PSU).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Udel® P-3700 HC is a high-clarity grade of polysulfone (PSU) that is nearly water-white in color. This grade was designed to eliminate the yellow cast and provide design flexibility and improved aesthetics for applications where a yellow cast is undesirable.Features: Acid Resistant; Alcohol Resistant; Alkali Resistant; Good Chemical Resistance; Good Toughness; High Clarity; High Heat Resistance; Hydrocarbon Resistant; Hydrolytically StableUses: Appliance Components; Appliances; Decorative Parts; Electrical/Electronic Applications; Food Service Applications; Medical/Healthcare Applications; Optical Applications; Safety EquipmentInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.30 %

@Time 86400 sec
0.30 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0070 cm/cm

@Thickness 3.18 mm
0.0070 in/in

@Thickness 0.125 in
Melt Flow 18 g/10 min

@Load 2.16 kg,
Temperature 343 °C
18 g/10 min

@Load 4.76 lb,
Temperature 649 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 75.8 MPa
11000 psi
ASTM D638
Elongation at Break 45 %
45 %
ASTM D638
Elongation at Yield 5.8 %
5.8 %
ASTM D638
Tensile Modulus 2.69 GPa
390 ksi
ASTM D638
Flexural Yield Strength 117 MPa
17000 psi
ASTM D790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 3.18 mm
0.993 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 56.0 µm/m-°C
31.1 µin/in-°F
Deflection Temperature at 1.8 MPa (264 psi) 178 °C

@Thickness 3.20 mm
352 °F

@Thickness 0.126 in
Annealed; ASTM D648
Glass Transition Temp, Tg 185 °C
365 °F
ASTM E1356
Optical Properties Metric English Comments
Refractive Index 1.635
1.635
ASTM D542
Haze 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D1003
Yellow Index 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D1925
Transmission, Visible 77 - 83 %

@Thickness 2.54 mm
77 - 83 %

@Thickness 0.100 in
ASTM D1003
Compliance Properties Metric English Comments
FDA Yes
Yes
Processing Properties Metric English Comments
Processing Temperature 149 °C
300 °F
Hopper
Melt Temperature 329 - 385 °C
624 - 725 °F
Mold Temperature 121 - 163 °C
250 - 325 °F
Drying Temperature 149 °C

@Time <=12600 sec
300 °F

@Time <=3.50 hour
Shot Size 50 - 75 %
50 - 75 %
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Colorless
Form Pellets
Processing Technique Extrusion; Injection Molding
RoHS Compliance RoHS Compliant