Solvay Specialty Polymers XydarÂ® G-930 Liquid Crystal Polymer (LCP), 30% Glass Fiber

Category	Polymer , Thermoplastic , Liquid Crystal Polymer (LCP)
Manufacturer	Solvay Specialty Polymers
Trade Name	Xydar®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers XydarÂ® G-930 Liquid Crystal Polymer (LCP), 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

XydarÂ® G-930 Liquid Crystal Polymer (LCP) is a glass reinforced injection molding grade developed specifically for electrical/electronic applications utilizing surface mount technology.The moldability of this resin is exceptional. XydarÂ® G-930 can fill very thin walls over long flow lengths with little or no flash, even at mold temperatures below 200Â°F (93Â°C). In addition, it has low warpage in molded products and exceptional weld line strength.Features: Flame Retardant; Good Chemical Resistance; Good Moldability; Good Weather Resistance; High Stiffness; High Strength; Low Warpage; Radiation (Gamma) ResistantUses: Automotive Applications; Automotive Electronics; Bobbins; Electrical Parts; Electrical/Electronic Applications; Industrial Applications; Industrial PartsAutomotive Specifications ASTM D5138 LCP0110 G30 B00000; DELPHI M-5282 M5282 Color: BK BlackInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.60 g/cc	0.0578 lb/inÂ³	ASTM D792
Filler Content	30 %	30 %	Glass Fiber
Water Absorption	<= 0.10 % @Time 86400 sec	<= 0.10 % @Time 24.0 hour	ISO 62

Mechanical Properties	Metric	English	Comments
Tensile Strength	135 MPa	19600 psi	ASTM D638
Elongation at Break	1.6 %	1.6 %	ASTM D638
Tensile Modulus	15.9 GPa	2310 ksi	ASTM D638
Flexural Strength	172 MPa	24900 psi	ASTM D790
Flexural Modulus	13.4 GPa	1940 ksi	ASTM D790
Izod Impact, Notched	0.960 J/cm	1.80 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.30 J/cm	8.06 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	3.60 - 7.20 Âµm/m-Â°C	2.00 - 4.00 Âµin/in-Â°F
CTE, linear, Transverse to Flow	40.0 - 79.0 Âµm/m-Â°C	22.2 - 43.9 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	271 Â°C	520 Â°F	Unannealed; ASTM D648
UL RTI, Electrical	220 Â°C @Thickness 0.750 mm	428 Â°F @Thickness 0.0295 in
UL RTI, Mechanical with Impact	200 Â°C @Thickness 0.750 mm	392 Â°F @Thickness 0.0295 in
UL RTI, Mechanical without Impact	220 Â°C @Thickness 0.750 mm	428 Â°F @Thickness 0.0295 in
Flammability, UL94	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	ASTM D150
	4.2 @Frequency 60.0 Hz	4.2 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	39.0 kV/mm @Thickness 1.57 mm	991 kV/in @Thickness 0.0618 in	ASTM D149
Arc Resistance	>= 300 sec	>= 300 sec	ASTM D495
Comparative Tracking Index	185 V	185 V	ASTM D3638

Processing Properties	Metric	English
Melt Temperature	321 - 360 Â°C	610 - 680 Â°F
Mold Temperature	65.6 - 93.3 Â°C	150 - 200 Â°F
Drying Temperature	149 Â°C @Time 21600 - 28800 sec	300 Â°F @Time 6.00 - 8.00 hour

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	North America
Clamp Tonnage	2.8 to 5.5 kN/cmÂ²
Color	Black; Natural
Form	Pellets
Processing Technique	Injection Molding
RoHS Compliance	RoHS Compliant
Screw Compression Ratio	2.5:1.0 to 3.0:1.0
Screw L/D Ratio	20.0:1.0 to 24.0:1.0