Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL A 118L V50 is a polyamide 6.6 reinforced with 50% of glass fiber, with thermal stability, UV protection and modified viscosity that provides better superficial appearance. Colors: it is marketed in the natural color. Special color can be produced on request.Main Properties: Excellent combination of thermal and mechanical properties under external environment (UV radiation); High fluency, that permits the injection mould of big dimension or complex geometric structures; Excellent dimensional stability; and Chemical stability Applications: TECHNYL A 118L V50 is a high performance product and is indicated for applications where the high mechanical and thermal resistance properties are request. Due these properties the TECHNYL A 118L V50 is very much request by automotive industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
100x100x3mm
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
100x100x3mm; 100x100x3mm
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785A
Tensile Strength at Break 220 MPa
31900 psi
ISO R 527
Elongation at Break 1.8 %
1.8 %
ISO R 527
Tensile Modulus 13.0 GPa
1890 ksi
ISO R 527
Flexural Strength 355 MPa
51500 psi
ISO 178
Flexural Modulus 16.78 GPa
2434 ksi
ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180/3A
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1D
Thermal Properties Metric English Comments
CTE, linear 2.70 µm/m-°C
1.50 µin/in-°F
ASTM D696
Melting Point 260 °C
500 °F
ASTM D3417
Deflection Temperature at 0.46 MPa (66 psi) >= 240 °C
>= 464 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) >= 240 °C
>= 464 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C
Mixing Zone 280-290°C