Material Notes:
Description: TECHNYL ® A 217 is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection molding. It is available in black color.Benefits: This product offers all the primary properties of unreinforced polyamide 66. In addition it has improved resistance to high temperature and it can be used for components which have to withstand mid term temperature stresses. This product can also be vacuum metalized with very good surface quality and adhesion of the aluminum surface. In case of fire its smoke rate is very low. It is also complying with NFF 16-101 rating I3 F2.Available in: Asia Pacific and EuropeRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applicationsApplications: It perfectly suits for the production of the head lamp bezels in automotive industry and connectors in electrical industry.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Water Absorption 1.3 %

@Temperature 23.0 °C,
Time 86400 sec
 1.3 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
1.5 %

@Temperature 100 °C,
Time 1800 sec
 1.5 %

@Temperature 212 °F,
Time 0.500 hour
 ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
ISO 527 Type 1A
Tensile Stress 59.0 MPa

@Strain 2.00 %
 8560 psi

@Strain 2.00 %
81.0 MPa

@Strain 4.00 %
 11700 psi

@Strain 4.00 %
83.0 MPa

@Strain 6.00 %
 12000 psi

@Strain 6.00 %
Tensile Strength, Yield 85.0 MPa
12300 psi
ASTM D638
88.0 MPa
12800 psi
ISO 527 type 1 A
Elongation at Break 20 %
20 %
ISO 527 Type 1A
30 %
30 %
ASTM D638
Tensile Modulus 3.30 GPa
479 ksi
ISO 527 Type 1A
Flexural Strength 125 MPa
18100 psi
ASTM D790
130 MPa
18900 psi
ISO 178
Flexural Modulus 3.10 GPa
450 ksi
ISO 178
3.50 GPa
508 ksi
ASTM D790
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/1A
80.0 kJ/m²
38.1 ft-lb/in²
ASTM D256
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 0.430 J/cm²
2.05 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75/Af
Flammability, UL94 V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
 1210
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
 1210
Oxygen Index 26 %
26 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 0.800 mm
 1200 °F

@Thickness 0.0315 in
 ISO 60695-2-12
650 °C

@Thickness 1.60 mm
 1200 °F

@Thickness 0.0630 in
 ISO 60695-2-12
650 °C

@Thickness 1.60 mm
 1200 °F

@Thickness 0.0630 in
 Ignition Temperature; ISO 60695-2-13
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C
Mixing Zone 280-290°C