Solvay TECHNYL® A 218G V30 PA66, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218G V30 PA66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA66, reinforced with 30% of glass fiber, for injection molding specially stabilized to improve its resistance automotive cooling liquids.Available in: Europe and Latin AmericaProduct Applications: TECHNYL® A 218 V43 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is commonly used in the automotive industry for engine components. This product is available in black. TECHNYL® A 218G V30 is particularly recommended for the injection molding of parts in permanent contact with cooling liquids in cars, such as:-cooling and heating radiator systems, header tanks, thermostat components, inlet/outlet pipes. This product is available in naturalInformation provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0062 cm/cm | 0.0062 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eU |
| 7.00 J/cm² @Temperature 120 °C, Time 720000 sec |
33.3 ft-lb/in² @Temperature 248 °F, Time 200 hour |
after aging water/glycol; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 700 °C @Thickness 1.60 mm |
1290 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+13 ohm-cm | 5.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |