Solvay TECHNYL® A 222 Black 1N PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 222 Black 1N PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide PA66, medium viscosity, heat stabilized, for injection molding, fast crystallization, for short cycles .Available in: EuropeProduct Applications: TECHNYL A 222 offers a good combination between primary properties of the unreinforced polyamide 66 and processing properties leading to increased productivity .These performances are associated with excellent dimensional stability and good rigidity of molded parts. This grade is used for connector parts in electrical and automotive industries. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0093 cm/cm | 0.0093 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 type 1 A |
| Elongation at Break | 20 % | 20 % | ISO 527 Type 1A |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 Type 1A |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 700 °C | 1290 °F | ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243 |
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution B; IEC 60112 |
| 575 V | 575 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-280°C |