Solvay TECHNYL® A 548B V15 PA66, 15% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 548B V15 PA66, 15% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 548B V15 is a copolyamide 6.6/6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: The product offers an excellent long term heat resistance and is suitable to work in environments characterized by a very high temperature.Available in: EuropeRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Thanks to its high melt strength, this product can be used to produce hollow parts, by suction blow molding technology, like tanks or ducts. Typical applications are turbo air ducts, especially inlet ducts up to 200°C.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183/A
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0098 cm/cm
0.0098 in/in
Linear Mold Shrinkage, Transverse 0.0098 cm/cm
0.0098 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527 Type 1A
Tensile Stress 30.0 MPa

@Strain 1.00 %
4350 psi

@Strain 1.00 %
85.0 MPa

@Strain 2.00 %
12300 psi

@Strain 2.00 %
90.0 MPa

@Strain 4.00 %
13100 psi

@Strain 4.00 %
92.0 MPa

@Strain 3.00 %
13300 psi

@Strain 3.00 %
Elongation at Break 5.0 %
5.0 %
ISO 527 Type 1A
Tensile Modulus 5.20 GPa
754 ksi
ISO 527 Type 1A
Flexural Strength 130 MPa
18900 psi
ISO 178
Flexural Modulus 4.10 GPa
595 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ISO 180/1eA
Izod Impact, Unnotched (ISO) 58.0 kJ/m²
27.6 ft-lb/in²
ISO 180/1eU
Charpy Impact Unnotched 6.80 J/cm²
32.4 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 242 °C
468 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75/Af
Processing Properties Metric English Comments
Feed Temperature 240 - 260 °C
464 - 500 °F
Adapter Temperature 245 - 265 °C
473 - 509 °F
Die Temperature 250 - 270 °C
482 - 518 °F
Head Temperature 250 - 270 °C
482 - 518 °F
Screw Cooling Temperature 245 - 265 °C
473 - 509 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 80.0 °C

@Time 28800 sec
176 °F

@Time 8.00 hour
dew point -35°C
Moisture Content <= 0.080 %
<= 0.080 %