Solvay TECHNYL® B 230 PA66/6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® B 230 PA66/6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced and modified copolyamide 66/6, with high flexibility and improved impact resistance, for injection molding.Available in: Asia Pacific and EuropeProduct Applications: TECHNYL ® B 230 is particularly recommended for applications where good impact resistance at low and room temperature is required , also for parts which could break during assembly or parts used at low humidity levels. This grade is commonly used in: automotive industry: bumpers and clips sports and leisure: sports bag buckles and electrical appliance: cable ties. This product is available in natural, black, and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183/A |
| Water Absorption | 1.35 % @Temperature 23.0 °C, Time 86400 sec |
1.35 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0107 cm/cm | 0.0107 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.022 cm/cm | 0.022 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0205 cm/cm | 0.0205 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 type 1 A |
| Elongation at Break | 50 % | 50 % | ISO 527 Type 1A |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 Type 1A |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 242 °C | 468 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Oxygen Index | 21 % | 21 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+13 ohm | 5.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 475 V | 475 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 250-260°C |