Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced with 45% of glass fiber, for injection molding.Available in: EuropeProduct Applications: TECHNYL C 216 V45 has been optimized to have high impact strength, a nice surface aspect and being easy to paint. It has been especially developed for the market of ski bindings, but can be advised as well for any part requiring a high rigidity as well as high impact strength. This product is available in natural and black colorsInformation provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183/A |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 Type 1A |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 Type 1A |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 475 V | 475 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 240-255°C |
Users viewing this material also viewed the following:
- Microcell Composite Company CELLOMER® 6000 SBS Rubber Pellets
- Lehmann & Voss LUVOCOM® 1105/XCF/20 PEEK, with carbon fiber
- Henkel Hysol PL 7000 Film Adhesive
- SABIC Innovative Plastics ULTEM 1100V PEI (Asia Pacific)
- Struktol CARSTAB® DSTDP Thioester Antioxidant
- SABIC Innovative Plastics Noryl LS175 PPE+HIPS
- Aremco Corr-Paint™ CP3015-GR High Temperature Protective Coating Inorganic, Mixed Oxides Filled
- Ashley Polymers Ashlene® 64M Nylon 66
- Covestro Makrofol® ID 6-2 Polycarbonate
- E-Polymers SEPAZ® N2020L Nanoclay 2% High flow Nano Composite Resin
Copyright © lookpolymers.com All Rights Reserved