Solvay Technyl® A 205F Nylon 66, EH0

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Technyl® A 205F Nylon 66, EH0.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the molding of long parts with thin wall sections, such as: cable tie, fasteners, and connectors.This product is available in natural, black and in colors on request.Glow wire test thick. 1,6 mm, IEC 695-2-1, 850°C.Information provided by Rhodia; Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183-A
Water Absorption 1.2 %
1.2 %
24 hours in water 23°C. ISO 62
Linear Mold Shrinkage 0.019 cm/cm
0.019 in/in
RHODIA-EP
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
RHODIA-EP
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 60.0 MPa
8700 psi
ISO 527
Tensile Strength, Yield 85.0 MPa
12300 psi
ISO 527
Elongation at Break 25 %
25 %
ISO 527
Elongation at Yield 4.0 %
4.0 %
ISO 527
Tensile Modulus 3.20 GPa
464 ksi
ISO 527
Flexural Yield Strength 120 MPa
17400 psi
ISO 178
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Izod Impact Resistance 0.450 J/cm²
2.14 ft-lb/in²
ISO 180
Charpy Impact Unnotched NB
NB
ISO 179/EU-1993
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
ISO 179/1EA-1993
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 185 °F
ASTM E831
Melting Point 263 °C
505 °F
ISO 3146-C
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75-2
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
ISO 1210/UL 94
V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
ISO 1210/UL 94
V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
ISO 1210/UL 94
Oxygen Index 28.5 %
28.5 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Surface Resistance 5.00e+14 ohm
5.00e+14 ohm
IEC 93
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 27.0 kV/mm
686 kV/in
IEC 243-1
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
IEC 250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 275 °C
518 - 527 °F
Middle Barrel Temperature 280 - 285 °C
536 - 545 °F
Front Barrel Temperature 285 - 290 °C
545 - 554 °F