Material Notes:
Luran 358 N is an easy-flowing injection molding SAN grade.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Melt Flow 22 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 22 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.0 MPa

@Temperature -40.0 °C
 13900 psi

@Temperature -40.0 °F
 ISO Data
Tensile Strength, Ultimate 72.0 MPa
10400 psi
5mm/min; ISO 527
Tensile Strength, Yield 72.0 MPa
10400 psi
2 in/min; ASTM Test
40.0 MPa

@Temperature 80.0 °C
 5800 psi

@Temperature 176 °F
 ISO Data
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
2.6 %

@Temperature -40.0 °C
 2.6 %

@Temperature -40.0 °F
 ISO Data
Elongation at Yield 2.1 %

@Temperature 80.0 °C
 2.1 %

@Temperature 176 °F
 ISO Data
Tensile Modulus 3.70 GPa
537 ksi
1mm/min; ISO 527
3.70 GPa
537 ksi
ASTM Test
Charpy Impact Unnotched 1.60 J/cm²
7.61 ft-lb/in²
ISO 179
1.60 J/cm²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179
Tensile Creep Modulus, 1 hour 3500 MPa
508000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 2800 MPa
406000 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 126 µm/m-°C
70.0 µin/in-°F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
annealed; ASTM Test
102 °C
216 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
annealed; ASTM Test
98.0 °C
208 °F
ISO 75
Vicat Softening Point 106 °C
223 °F
Rate "A" Loading 1 (50 degC/h 10N); ASTM Test
106 °C
223 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
Oxygen Index 18 %
18 %
ISO 4589-1/-2
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
unknown thickness
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
 2.7

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 100 Hz
 0.0040

@Frequency 100 Hz
 IEC 60250
0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 400 V
400 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 230 °C
446 °F
Injection molding
Mold Temperature 50.0 °C
122 °F
Injection molding
Injection Velocity 200 mm/sec
7.87 in/sec
Injection molding
Descriptive Properties Value Comments
Color Clear
Commercial Status North America and Europe
FDA Yes
Form Pellets
Impact Modified No
NSF Std. 51 No
NSF Std. 61 No
Primary Processing Technique Injection Molding
Processing Injection Molding
UL.UL-C Yes