Styrolution Luran® HH-120 Alpha-Methylstyrene Acrylonitrile

Category Polymer , Thermoplastic , SAN Polymer
Manufacturer Styrolution
Trade Name Luran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® HH-120 Alpha-Methylstyrene Acrylonitrile.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Luran HH-120 is a grade of AMSAN with high heat resistance and improved mechanical strength. It is suitable for injection molding and extrusion applications and can be used as a modifier for high heat ABS and PVC.Outstanding heat resistanceVery good mechanical strengthGood surface appearanceExcellent dimensional stabilityNew SPF 50 UV stabilization availableInformation provided by Styrolution
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.30 %

@Temperature 23.0 °C
0.30 %

@Temperature 73.4 °F
50% RH; ISO 62
Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
ISO 294-4
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 84
84
Ball Indentation Hardness 175 MPa
25400 psi
ISO 2039-1
Tensile Strength, Yield 79.0 MPa
11500 psi
ISO 527
Elongation at Yield 3.0 %
3.0 %
ISO 527
Tensile Modulus 3.90 GPa
566 ksi
ISO 527
Flexural Strength 135 MPa
19600 psi
ISO 178
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature 23.0 °C
0.952 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
Charpy Impact Unnotched 2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179
2.10 J/cm²

@Temperature -30.0 °C
9.99 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
DIN 52612-1
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
ISO 75
Vicat Softening Point 120 °C

@Load 5.10 kg
248 °F

@Load 11.2 lb
50°C/h; ISO 306
Optical Properties Metric English Comments
Refractive Index 1.567
1.567
Sodium D Line; ASTM D 542
Transmission, Visible >= 89 %

@Wavelength 550 nm
>= 89 %

@Wavelength 550 nm
ASTM D 1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Melt Temperature 220 - 270 °C
428 - 518 °F
ISO 294
Mold Temperature 60.0 °C
140 °F
ISO 294
Injection Velocity 200 mm/sec
7.87 in/sec
ISO 294
Drying Temperature 80.0 °C

@Time 7200 - 14400 sec
176 °F

@Time 2.00 - 4.00 hour